DuPont Performance Polymers Delrin® 127UVE NC010 Acetal Homopolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 127UVE NC010 Acetal Homopolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® 127UVE NC010 (formerly DE20555) is a high viscosity acetal homopolymer with UV stabilizers having extremely low VOC emissions, developed for automotive interior applications.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.50 %

@Temperature 23.0 °C
0.50 %

@Temperature 73.4 °F
Immersion 24h; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.021 cm/cm

@Thickness 2.00 mm
0.021 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.019 cm/cm

@Thickness 2.00 mm
0.019 in/in

@Thickness 0.0787 in
ISO 294-4
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Melt Index of Compound 2.1 g/10 min
2.1 g/10 min
cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 71.0 MPa

@Temperature 23.0 °C
10300 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 45 %

@Temperature 23.0 °C
45 %

@Temperature 73.4 °F
nominal; ISO 527
65 %

@Temperature 23.0 °C
65 %

@Temperature 73.4 °F
50mm/min; ISO 527
Elongation at Yield 28 %

@Temperature 23.0 °C
28 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 2.90 GPa

@Temperature 23.0 °C
421 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 2.80 GPa

@Temperature 23.0 °C
406 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact Unnotched 34.0 J/cm²

@Temperature -30.0 °C
162 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
39.0 J/cm²

@Temperature 23.0 °C
186 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.40 J/cm²

@Temperature 23.0 °C
6.66 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
278 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
278 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 100 °C
278 µin/in-°F

@Temperature 131 - 212 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
50.0 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
110 µm/m-°C

@Temperature 23.0 - 55.0 °C
61.1 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
150 µm/m-°C

@Temperature 55.0 - 100 °C
83.3 µin/in-°F

@Temperature 131 - 212 °F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 91.0 °C
196 °F
ISO 75-1/-2
Processing Properties Metric English Comments
Melt Temperature 205 °C
401 °F
Optimum; Injection Molding
200 - 210 °C
392 - 410 °F
Injection Molding
Mold Temperature 90.0 °C
194 °F
optimum; Injection Molding
80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Moisture Content <= 0.20 %
<= 0.20 %
Injection Molding
Descriptive Properties Value Comments
Appearance Natural Color
Forms Pellets
Generic POM
Material Status Preliminary Data
Part Marking Code >POM<
ISO 11469
Polymer Family POM
Polymer Type POM Homopolymer
Processing Method Injection Molding
Product Category Low Emissions Resins
Unreinforced Resins
UV Resistant/Weatherable Resins
Region Available - Global Yes
Resin Identification POM
ISO 1043
RoHS Compliance Contact Manufacturer
Uses automotive interior applications
Copyright © lookpolymers.com All Rights Reserved