- Polykemi AB POLYelast TPE R44 T10 Thermoplastic Elastomer, Mineral Reinforced
Polykemi AB POLYelast TPE R44 T10 Thermoplastic Elastomer, Mineral Reinforced
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE R44 T10 Thermoplastic Elastomer, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 |
| 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | With Flow; ISO 2577 | |
| Melt Index of Compound | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 54 @Time 15.0 sec |
54 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 19.0 MPa | <= 2760 psi | ISO/R527 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO/R527 |
| Flexural Strength | <= 25.0 MPa | <= 3630 psi | ISO 178 |
| Flexural Modulus | 0.750 GPa @Temperature 23.0 °C |
109 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -20.0 °C |
7.14 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 2.80 J/cm² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 132 °C @Load 1.00 kg |
270 °F @Load 2.21 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | |
| Mold Temperature | 20.0 - 60.0 °C | 68.0 - 140 °F | |
| Injection Pressure | 90.0 - 110 MPa | 13100 - 16000 psi | |
| Back Pressure | 0.200 - 0.500 MPa | 29.0 - 72.5 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® TD-9022-D Super Hexene Film Resin
- Flint Hills P5M6K-080 Polypropylene Random Copolymer
- Haynes HR-160® alloy, hot rolled and solution annealed plate
- Samsung Cheil Industries Infino® HF-3200H PC, Glass Filled High Impact
- TIMCAL TIMREX® HSAG400 Primary Synthetic High Surface Graphite
- A. Schulman COMTUF® 506 Polycarbonate
- Zylog Hipolyene® 7635 MI Thermoplastic Polyolefin & PP Compound
- Lubrizol Estane® 2103-55D Thermoplastic Polyurethane Elastomer
- A. Schulman ComAlloy Hiloy® 623 Nylon 6/6, Glass Reinforced, Flow Enhanced, UL
- 3M Controltac™ IJ180-10 Graphic Film
Copyright © lookpolymers.com All Rights Reserved