SABIC Innovative Plastics LNP THERMOCOMP MK0049A PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MK0049A PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STARFLAM* MK0049A is a compound based on Polypropylene resin containing Talc, Flame Retardant. Added features include : Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 2.6 % | 2.6 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 37.0 MPa | 5370 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.90 GPa | 421 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 82.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
45.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 128 µm/m-°C @Temperature 23.0 - 60.0 °C |
71.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Ovation Polymers Optrene 10GF Polypropylene
- Samsung Cheil Industries Infino® ASF-9810F PBT/PET, Mineral Filled General Purpose
- Styron CALIBREâ„¢ 340 TNIR Polycarbonate Resin
- UBE UBESTA® 3024LU Rigid Black Electronic Grade Nylon 12
- Wellman Wellamid® 22L-NBK1 Engineering Grade Nylon 66
- A. Schulman COMTUF® 462 Glass/Fiber Mineral Reinforced, Impact Modified PET Alloy
- Universal Wire Works No. 6 Cobalt Alloy Welding Wire
- 3M 12062 Black 3/32" (2.4 mm) Polyurethane Foam
- PPT BP125HR NiZn Ferrite Powder
Copyright © lookpolymers.com All Rights Reserved