SABIC Innovative Plastics LNP THERMOCOMP TH0750A PUR (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP TH0750A PUR (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* TH0750A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.50 g/cc | 0.271 lb/in³ | ASTM D792 |
| 7.50 g/cc | 0.271 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.160 % | 0.160 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527 |
| 19.0 MPa | 2760 psi | ASTM D638 | |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ISO 527 |
| 19.0 MPa | 2760 psi | ASTM D638 | |
| Elongation at Break | 5.3 % | 5.3 % | ISO 527 |
| 30.1 % | 30.1 % | ASTM D638 | |
| Elongation at Yield | 4.8 % | 4.8 % | ISO 527 |
| 21.9 % | 21.9 % | ASTM D638 | |
| Tensile Modulus | 1.16 GPa | 168 ksi | 50 mm/min; ASTM D638 |
| 1.62 GPa | 235 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 25.0 MPa | 3630 psi | ASTM D790 |
| 26.0 MPa | 3770 psi | ISO 178 | |
| Flexural Modulus | 1.39 GPa | 202 ksi | ASTM D790 |
| 1.68 GPa | 244 ksi | ISO 178 | |
| Izod Impact, Notched | 1.73 J/cm | 3.24 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.02 J/cm | 26.27 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 77.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C @Thickness 3.20 mm |
167 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 46.0 °C @Thickness 3.20 mm |
115 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Pasargad Polymer Peyvand Pasalen 3P-H3130B Polypropylene, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP COLORCOMP JX91550 PES (Asia Pacific)
- LATI Latigloss 66 H2 G/50 F2 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized
- Samsung Cheil Industries Starex® VB-4921 ABS, Glass Filled FR
- Styron Magnumâ„¢ 8325 ABS, Sheet Coextrusion Grade
- Saint-Gobain CHR® C665 Copper Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- Wanhua Chemical Wanthane® WHT-1195 Polyester Based TPU
- Elastocon TPE Technologies Elastocon® STK60X Thermoplastic Elastomer
- Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Dry)
- Bapolene® 4062NA Polypropylene, Injection Grade
Copyright © lookpolymers.com All Rights Reserved