Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

SABIC Innovative Plastics LNP Thermocomp 9X06477 SPS

Category Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp 9X06477 SPS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* 9X06477 is a compound based on Syndiotactic Polystyrene resin containing Glass Fiber. Characteristics of this grade is Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
1.21 g/cc
0.0437 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.080 %
0.080 %
23°C / 50% RH; ISO 62
0.060 %

@Time 86400 sec
 0.060 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Time 86400 sec
 0.0030 - 0.0050 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
Type I, 5 mm/min; ASTM D 638
80.0 MPa
11600 psi
5 mm/min; ISO 527
Elongation at Break 1.0 %
1.0 %
Type I, 5 mm/min; ASTM D 638
1.1 %
1.1 %
5 mm/min; ISO 527
Tensile Modulus 7.97 GPa
1160 ksi
1 mm/min; ISO 527
8.57 GPa
1240 ksi
50 mm/min; ASTM D 638
Flexural Strength 117 MPa
17000 psi
1.3 mm/min, 50 mm span; ASTM D 790
127 MPa
18400 psi
ISO 178
Flexural Modulus 7.45 GPa
1080 ksi
2 mm/min; ISO 178
7.69 GPa
1120 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.460 J/cm

@Temperature 23.0 °C
 0.862 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 3.13 J/cm

@Temperature 23.0 °C
 5.86 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 17.0 kJ/m²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
3.00 J

@Temperature 23.0 °C
 2.21 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 39.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 21.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 48.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 26.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 238 °C
460 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
247 °C

@Thickness 3.20 mm
 477 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
219 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
129 °C

@Thickness 3.20 mm
 264 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved