Plastcom SLOVALEN PH 79 GF 20 Polypropylene Homopolymer, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVALEN PH 79 GF 20 Polypropylene Homopolymer, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 20% glass fiber, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, modulus in tension due to the modification. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.0177 cm/cm | 0.0177 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0189 cm/cm | 0.0189 in/in | STN 64 0808 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | STN EN ISO 527-2 |
| Elongation at Break | 3.0 % | 3.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 4.60 GPa | 667 ksi | STN EN ISO 527-2 |
| Flexural Strength | 80.0 MPa | 11600 psi | STN EN ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 3.30 J/cm² @Temperature -20.0 °C |
15.7 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | STN EN ISO 75/A |
| Vicat Softening Point | 135 °C | 275 °F | B; STN EN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | |
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi |
Users viewing this material also viewed the following:
- Parabeam Industrie Paraglass 3 3D Glass Fabric
- SABIC Innovative Plastics NORYL V0150B PPE+HIPS (Asia Pacific)
- Silberline Sparkle Silvet® Premier 890-30-E1
- Polyplastics Duranex® 6300B Polybutylene Terephthalate (PBT), Anisotropy improvement, 30% GB filled
- CP-Polymer-Technik Wellamid® 6000 MRGV 20/10 HWCP 20% Mineral and 10% Glass Fiber Nylon 6, Heat Stabilized, Dry
- Ametek P434L P/M Stainless Steel, Sintered from 6.2 g/cc Green Density
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N220 Filler
- A. Schulman POLYFORT™ FPP 3711 High Impact Polypropylene
- PolyOne Geon™ Vinyl Wire & Cable W3301 Polyvinyl Chloride, Flexible (PVC, Flexible)
Copyright © lookpolymers.com All Rights Reserved