Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
Polycasa PC QUINN PC sheets have excellent optical properties and a brilliant surface. The QUINN PC range contains sheets that are easy to fabricate and show exceptional performance at both low and high tempera.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
Network Polymers Kepital® F10-02 Description: Natural Acetal CopolymerInformation provided by Network Polymers Inc. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® EFX830ME PC Flame retardant modified PC blend using non-brominated and non-chlorinated flame retardant systems, offering metallic / sparkle look with minimal flow line visibilityThis data was supplied by SABIC-.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
Nilit FRIANYL A63 N-S20 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, low viscosity, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | <= 60.0 MPa | <= 8700 psi | ISO/R527 |
Polykemi AB SCANTEC PC S75R V0 Polycarbonate, Flame Retardant Information provided by Polykemi AB |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
Polymer Resources PC-FR1-D Polycarbonate, Improved Flame Retardant, Low Flow Polycarbonate, Improved Flame Retardant, Low FlowFeatures: • High Impact Resistance • High Viscosity • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal t.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD1711 PC Copolymer 25 MFR LEXAN High Flow Ductile Copolymer |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® XHT2141 PC Copolymer XHT2141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® XHT2146 PC Copolymer XHT2146 resin is a high flow, high heat polycarbonate copolymer with improved release performance compared to Lexan* XHT2141 resin. It is available in a range of opaque and limited transparent colo.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® XHT2146 PC Copolymer (Europe-Africa-Middle East) XHT2146 resin is a high flow, high heat polycarbonate copolymer with improved release performance compared to Lexan* XHT2141 resin. It is available in a range of opaque and limited transparent colo.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP FARADEX NX07344 PC+ABS (Asia Pacific) Faradex NX07344 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel and glass fiber. Added features of this material incl.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® 945U PC (Europe-Africa-Middle East) Lexan* 945U Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is UV stabilized, providing additio.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | 10% MS0825 addition (vs. 30 MPa for neat Nylon 6) |
Hybrid Plastics MS0825 Nanoreinforced® POSS® Polyamide 6 Nanoreinforced® polyamide 6 (PA6) utilizes POSS® technology to achieve increased hydrophobicity, increased oil resistance, improved toughness and easier processability through structural contr.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® BKV 15 H2.0 901510 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, good heat-ageing resistance |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | |
LATI Latan 9 POM Polyoxymethylene (POM). Unfilled. Medium viscosity. Very good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by La.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL V0150B PPE+HIPS (Europe-Africa-Middle East) Noryl* V0150B is an unfilled, injection moldable modified polyphenylene ether resin.. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 1.5 mm a.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® X4850 PBT+PC (Europe-Africa-Middle East) Xenoy X4850 is a hydrostable, high modulus, high ductile PC/PBT blend. Furthermore, this resin provides high chemicalresistance, very low creep, low CTE, excellent fatique and high heat dimensional .. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics XYLEX X8409AC PC+POLYESTER (Europe-Africa-Middle East) PC + Polyester, Injection (Blow) Molding, or Extrusion Blow molding grade, Chemical Resistance and Transparency |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl GTX GTX965 PPE+PA66 NORYL GTX965 is a mineral reinforced PPE/PA blend. It offers excellent surface appearance, processability and dimensional stability at elevated temperatures. The best molding condition for good appe.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66 NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Asia Pacific) PPE+PS blend. 10% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including wate.. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D 638 |
Cossa Polimeri ESTACARB 0400 OPALE Polycarbonate Polycarbonate for injection or extrusionOpal, light diffusiveInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
Entec Hylex® P1017FR Polycarbonate Information provided by Ravago. |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339G25M5CL Glass/Mineral Reinforced Coupled |
|||
Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO R 527 |
Addiplast Addinyl B2 E Flame Retardant Nylon 6 Flame retardant, halogen freeInformation provided by Addiplast. |
|||
Tensile Strength at Break | 60.0 MPa @Temperature 120 °C |
8700 psi @Temperature 248 °F |
ISO Data |
BASF Ultramid® 8233G HS BK-106 33% Glass Filled PA6 (Conditioned) Ultramid 8233G HS BK-106 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature
performance and .. |
|||
Tensile Strength at Break | 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® ET-1000 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel ET-1000 HS is an impact modified, heat stabilized polyphthalamide (PPA) that exhibits exceptional impact strength and toughness. Like all Amodel PPA resins, ET-1000 HS offers high fatigue str.. |