Cossa Polimeri ESTACARB 0400 OPALE Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Extruded , Polycarbonate, Molded |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTACARB |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTACARB 0400 OPALE Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate for injection or extrusionOpal, light diffusiveInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D 638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ASTM D 638 |
| Elongation at Break | >= 50 % | >= 50 % | ASTM D 638 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D 790 |
| Izod Impact, Notched | 5.00 J/cm @Temperature 0.000 °C |
9.37 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 6.00 J/cm @Temperature 23.0 °C |
11.2 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 135 °C | 275 °F | I.E.C. 335-1 |
| Vicat Softening Point | 145 °C @Load 5.00 kg |
293 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 150 °C @Load 0.999 kg |
302 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
||
| Glow Wire Test | 850 °C @Thickness 2.00 mm |
1560 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- PolyOne Trilliant™ HC X HC5200-0026 RS Natural Polypropylene, Unspecified (PP, Unspecified)
- Premix Thermoplastics PRE-ELEC® PE 1291
- SABIC Innovative Plastics Lexan® 923A PC (Asia Pacific)
- Eastman Eastalloy DA003 PC+PCTG Copolyester/Polycarbonate (discontinued **)
- Polykemi AB POLYfill PPC T8020 FC Polypropylene Copolymer, Mineral Reinforced
- ICO Polymers ICORENEâ„¢ 195-4060 LMDPE Rotational Molding Resin
- LG Chemical SEETEC H1500 Polypropylene Homopolymer
- Covestro Apec® 1805 Polycarbonate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved