Lanxess DurethanÂ® BKV 15 H2.0 901510 Copolyamide, 15% Glass Fiber

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	Lanxess
Trade Name	Durethan®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lanxess DurethanÂ® BKV 15 H2.0 901510 Copolyamide, 15% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CoPA, injection molding grade, 15% glass fibers, good heat-ageing resistance

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/inÂ³	ISO 1183
Water Absorption	8.5 %	8.5 %	Test Sim. to ISO 62
Moisture Absorption at Equilibrium	2.6 %	2.6 %	23Â°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test	138 cmÂ³/g	138 cmÂ³/g	Viscosity number; ISO 307, 1157, 1628

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	Conditioned; ISO 527-1/-2
	125 MPa	18100 psi	ISO 527-1/-2
Elongation at Break	2.5 %	2.5 %	ISO 527-1/-2
	15 %	15 %	Conditioned; ISO 527-1/-2
Tensile Modulus	3.20 GPa	464 ksi	Conditioned; ISO 527-1/-2
	6.20 GPa	899 ksi	ISO 527-1/-2
Charpy Impact Unnotched	4.00 J/cmÂ² @Temperature -30.0 Â°C	19.0 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eU
	4.50 J/cmÂ² @Temperature -30.0 Â°C	21.4 ft-lb/inÂ² @Temperature -22.0 Â°F	Conditioned; ISO 179/1eU
	5.00 J/cmÂ² @Temperature 23.0 Â°C	23.8 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eU
	9.00 J/cmÂ² @Temperature 23.0 Â°C	42.8 ft-lb/inÂ² @Temperature 73.4 Â°F	Conditioned; ISO 179/1eU
Charpy Impact, Notched	<= 1.00 J/cmÂ² @Temperature -30.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	<= 1.00 J/cmÂ² @Temperature -30.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature -22.0 Â°F	Conditioned; ISO 179/1eA
	<= 1.00 J/cmÂ² @Temperature 23.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA
	<= 1.00 J/cmÂ² @Temperature 23.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature 73.4 Â°F	Conditioned; ISO 179/1eA
Impact	613	613	Puncture maximum force (N); ISO 6603-2
	608 @Temperature -30.0 Â°C	608 @Temperature -22.0 Â°F	Puncture maximum force (N); ISO 6603-2
Puncture Energy	1.80 J	1.33 ft-lb	ISO 6603-2
	7.80 J	5.75 ft-lb	Conditioned; ISO 6603-2
	1.80 J @Temperature -30.0 Â°C	1.33 ft-lb @Temperature -22.0 Â°F	ISO 6603-2
	1.80 J @Temperature -30.0 Â°C	1.33 ft-lb @Temperature -22.0 Â°F	Conditioned; ISO 6603-2

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	30.0 Âµm/m-Â°C	16.7 Âµin/in-Â°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	80.0 Âµm/m-Â°C	44.4 Âµin/in-Â°F	ISO 11359-1/-2
Melting Point	213 Â°C	415 Â°F	10Â°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	210 Â°C	410 Â°F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	190 Â°C	374 Â°F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	60.0 Â°C	140 Â°F	ISO 75-1/-2
Vicat Softening Point	200 Â°C	392 Â°F	50Â°C/h 50N; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 60695-11-10
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in	IEC 60695-11-10
Oxygen Index	22 %	22 %	ISO 4589-1/-2

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	375 V	375 V	IEC 60112

Descriptive Properties	Value	Comments
Additives	Release agent
Features	Heat stabilized or stable to heat
Form	Pellets
ISO Shortname	ISO 1874-PA 6/66, MHR, 14-050, GF15
Processing	Injection molding