- Polymer Property : Tensile Strength at Break = 4790 psi
Polymer Property : Tensile Strength at Break = 4790 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.0 MPa | 4790 psi | |
| Plastcom SLOVALEN PH 22 T 40 PP, 40% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, chemically modified talc. Special designed for automotive light housings. Delivered in natural mo.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® EX75 ABS Multi-purpose, extrusion ABS providing a favorable balance of engineering properties. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® FR30U ABS (Asia Pacific) Flame retardant ABS. Good indoor UV properties. Excellent moldability with no bloom. V-1/V-0/5VB rated. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® MG38F ABS Very high impact ABS. Toughness/rigidity. FDA compliant. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® MG47 ABS Multi-purpose, injection molding ABS providing a favorable balance of engineering properties. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® MG47F ABS Multi-purpose, injection molding ABS providing a favorable balance of engineering properties. FDA compliant. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics GELOY CR8510 ASA ASA with outstanding UV exposure performance for both exterior and interior applications. F1 Rated. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP COLORCOMP A1000H ABS LNP* COLORCOMP* A1000H is an unfilled compound based on ABS. Added feature of this grade is: Healthcare. |
|||
| Tensile Strength at Break | <= 33.0 MPa | <= 4790 psi | ISO/R527 |
| Polykemi AB POLYfill PPH T3022D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics GELOY CR7500 ASA (Europe-Africa-Middle East) High heat ASA with optimum flow-impact balance. For Automotive applications and Automotive colors only. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Geloy XTWE280 ASA (Asia Pacific) Weatherble ASA profile extrusion gradeThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527 |
| Total Evatane® 28 - 03 HDPE, blown film
(discontinued **) EVA Copolymer made by high pressure tubular process. Temperature profile (°C) for injection molding: 130 to 160.Information provided provided by Total Petrochemicals.Total Petrochemicals includes f.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 |
| Braskem HM 150 HDPE Monofilament Polyethylene
(discontinued **) Applications: Raschel; flat yarn; general and industrial rape netting. Information provided by Braskem |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO R 527 |
| Fainplast Compounds RK 320 Rigid PVC, Extrusion Lead Free Indoor profiles |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing 20% Milled Glass, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP LNP LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing 20% Glass Fiber and 15% PTFE. Added features of this material include: Heat Stabilized, Low Extractable, Wear Resistant... |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Europe-Africa-Middle East) LNP* Stat-Loy* A30009 is a compound based on Acrylonitrile Butadiene resin, containing Proprietary Filler, Flame Retardant. Added features include : Permanent Antistatic, Flame retardant. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 0.2 in/min; ASTM Test |
| Styrolution Terblend® N NM-12 ABS/PA6 (Conditioned) Terblend N NM-12 is an ABS/PA6 blend combining high impact strength and rigidity with an excellent processability and surface appearance.Information provided by STYROLUTION, which is a joint venture.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL PPX PPX7112 PPE+PP PPE+PP blend. Suitable for painted exterior automotive applications. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Crosshead speed 100 mm/min; ISO 527 |
| SCG Chemicals EL-Leneâ„¢ H5211PC High Density Polyethylene Pipe Resin Key Characteristics: Good processing, high thermal stability, good balance of MRS, SCG, and RCPRecommended Applications: Water pressure and gas pipesCertification: Certified by EXOVA, LNE, AENOR,.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | |
| UBE C (Low-Cis) HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBE high impact polystyrene (HIPS).Information provided by UBE. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527-1/-2 |
| DuPont Performance Polymers Hytrel® G5544 Polyester Elastomer TPC-ET
(Unverified Data**) 55 Shore D Standard Performance Polyester Elastomer with Heat Ageing ProtectionHytrel G5544 is a medium modulus grade with nominal hardness of 55D. It contains discoloring stabilizer. It can be proc.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0339G5M25CL Glass/Mineral Reinforced Coupled |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM-D638 |
| Braskem TN2006 EVA General Film Copolymer TN2006 is an Ethylene-Vinyl Acetate (EVA) copolymer with good mechanical properties, high flexibility and toughness even with low temperature, and excellent optical and heat sealability properties. .. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO R 527 |
| Addiplast Addilene H 652 Polypropylene Homopolymer High temperature resistance, high gloss, very good surface appearanceInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527 |
| Bulk Molding Compounds BMC 665 Mineral filled, 20% glass reinforced polyester molding compound Description: BMC 665 molding compound is a mineral filled, glass reinforced polyester molding compound suitable for compression, transfer or stuffer injection molding. It is characterized by good.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | |
| Plastcom SLOVALEN PH 21 T 20 PP, 20% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shr.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Conditioned; ISO R 527 |
| Addiplast Addilene PMD 50203 Flame Retardant Polypropylene Flame retardant, unreinforced, with halogensInformation provided by Addiplast. |
|||