SABIC Innovative Plastics NORYL PPX PPX7112 PPE+PP
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl PPX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PPX PPX7112 PPE+PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PP blend. Suitable for painted exterior automotive applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10.5 g/10 min @Load 5.00 kg, Temperature 260 °C |
10.5 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.17 GPa | 170 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 49.0 MPa | 7110 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.34 GPa | 194 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 37.0 J @Temperature 23.0 °C |
27.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 155 µm/m-°C @Temperature -40.0 - 40.0 °C |
86.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 85.0 °C | 185 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.52 mm |
HB @Thickness 0.0598 in |
UL 94 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO-LOCK SERIES 11-HT Anaerobic Thread Locking Compound
- Polykemi AB POLYabs HF0 ABS
- ExxonMobil Escorene® LD-336 EVA Film Resin, Clarity, Very High Drawdown (discontinued **)
- Materion BrushCAST® 165C High Strength Casting Alloy (As Cast & Aged)
- Mitsubishi Xantar® FC 25 R Polycarbonate
- Terio Corporation TZY-3 Yttria Stabilized Zirconia
- Cytec EN-12 (Conap) Casting, Potting, and Molding Compound
- Equate EPDA-5040 HDPE Non-Pressure Gravity Pipe Resin
- Total Finaprene® 1205 Di-block Styrene-Butadiene TPE Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved