SABIC Innovative Plastics Cycolac® EX75 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® EX75 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Multi-purpose, extrusion ABS providing a favorable balance of engineering properties.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Viscosity | 1.16e+6 cP | 1.16e+6 cP | Melt Viscosity, 240°C, 100 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 42.9 % | 42.9 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.13 GPa | 309 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 4.21 J/cm | 7.89 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 35.0 J @Temperature 23.0 °C |
25.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C @Thickness 3.20 mm |
201 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 106 °C | 223 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N85U Nitrile Rubber
- Polycasa XT Soft Tone PMMA
- Karina E 1000/3055-IE MBPEB White Color Concentrate
- SABIC Innovative Plastics PC0800 PC
- SABIC Innovative Plastics LNP LUBRICOMP OX97635 PPS
- SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East)
- Chosun Refractories CRS-A60 Blast Furnace Tap-Hole Refractory
- CMW® ELKONITE® TC53 Heat Treatable Tungsten Carbide Copper material
- Addiplast Addilene J 690 RM20F Flame Retardant Polypropylene, 20% Mineral Filled
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 330ºF Cure Temperature
Copyright © lookpolymers.com All Rights Reserved