SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing 20% Glass Fiber and 15% PTFE. Added features of this material include: Heat Stabilized, Low Extractable, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| 36.0 MPa | 5220 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527 |
| 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.1 % | 1.1 % | 5 mm/min; ISO 527 |
| 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.32 GPa | 772 ksi | 1 mm/min; ISO 527 |
| 5.73 GPa | 831 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 59.0 MPa | 8560 psi | ISO 178 |
| Flexural Yield Strength | 61.0 MPa | 8850 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.48 GPa | 650 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.58 GPa | 664 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.410 J/cm | 0.768 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.51 J/cm | 2.83 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GF 1200 33 Red 31 A Polyamide 66 (Nylon 66)
- Pyrotek Pyrotherm M-68 Structural Insulation Board
- Henkel Alodine 1132 Touch-N-Prep Coating Touch-Up Conversion Coating
- Techmer ES HiFill FR® ABS GB10 FR 10% Glass Bead Filled
- Wieland 1408 Wilaform Gold
- A. Schulman SCHULADUR® B GF15 15% Glass Fiber Reinforced PET
- ExxonMobil Santoprene® 151-70W256 Thermoplastic Vulcanizate - Flame Retardant
- Fainplast Compounds HAX HF 200 Halogen Free PVC
- ChevronTexaco Aries® 46
- Fainplast Compounds PG 56/B Flexible PVC, Extrusion Modified with Rubber
Copyright © lookpolymers.com All Rights Reserved