DuPont Performance Polymers Hytrel® G5544 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® G5544 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
55 Shore D Standard Performance Polyester Elastomer with Heat Ageing ProtectionHytrel G5544 is a medium modulus grade with nominal hardness of 55D. It contains discoloring stabilizer. It can be processed by many conventional thermoplastic processing teInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
1.22 g/cc
0.0441 lb/in³
ISO 1183
Water Absorption 2.2 %

@Thickness 2.00 mm
 2.2 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.400 %

@Thickness 2.00 mm
 0.400 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 1.6 %
1.6 %
Immersion 24h; ASTM D570
Viscosity 56910 cP

@Shear Rate 5000 1/s,
Temperature 255 °C
 56910 cP

@Shear Rate 5000 1/s,
Temperature 491 °F
 ISO 11403-1 -2
61310 cP

@Shear Rate 5000 1/s,
Temperature 245 °C
 61310 cP

@Shear Rate 5000 1/s,
Temperature 473 °F
 ISO 11403-1 -2
69010 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 69010 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
202800 cP

@Shear Rate 500 1/s,
Temperature 255 °C
 202800 cP

@Shear Rate 500 1/s,
Temperature 491 °F
 ISO 11403-1 -2
227840 cP

@Shear Rate 500 1/s,
Temperature 245 °C
 227840 cP

@Shear Rate 500 1/s,
Temperature 473 °F
 ISO 11403-1 -2
271700 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 271700 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 cm³/10min; ISO 1133
10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 51
51
15s; ISO 868
<= 56
<= 56
ISO 868
Tensile Strength at Break 33.0 MPa
4790 psi
ISO 527-1/-2
Tensile Stress 8.10 MPa

@Strain 5.00 %
 1170 psi

@Strain 5.00 %
 ISO 527-1/-2
9.00 MPa

@Strain 50.0 %
 1310 psi

@Strain 50.0 %
 ISO 527-1/-2
11.7 MPa

@Strain 10.0 %
 1700 psi

@Strain 10.0 %
 ISO 527-1/-2
4.13 MPa

@Strain 6.80 %,
Temperature 120 °C
 599 psi

@Strain 6.80 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.22 MPa

@Strain 7.50 %,
Temperature 100 °C
 757 psi

@Strain 7.50 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.35 MPa

@Strain 6.00 %,
Temperature 90.0 °C
 776 psi

@Strain 6.00 %,
Temperature 194 °F
 ISO 11403-1 -2
5.46 MPa

@Strain 7.15 %,
Temperature 90.0 °C
 792 psi

@Strain 7.15 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.19 MPa

@Strain 16.83 %,
Temperature 120 °C
 898 psi

@Strain 16.83 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.87 MPa

@Strain 7.36 %,
Temperature 60.0 °C
 996 psi

@Strain 7.36 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
6.88 MPa

@Strain 26.86 %,
Temperature 120 °C
 998 psi

@Strain 26.86 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.16 MPa

@Strain 36.88 %,
Temperature 120 °C
 1040 psi

@Strain 36.88 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.31 MPa

@Strain 46.91 %,
Temperature 120 °C
 1060 psi

@Strain 46.91 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.44 MPa

@Strain 60.51 %,
Temperature 120 °C
 1080 psi

@Strain 60.51 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.53 MPa

@Strain 17.5 %,
Temperature 100 °C
 1090 psi

@Strain 17.5 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.57 MPa

@Strain 73.4 %,
Temperature 120 °C
 1100 psi

@Strain 73.4 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.73 MPa

@Strain 87.01 %,
Temperature 120 °C
 1120 psi

@Strain 87.01 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.90 MPa

@Strain 6.00 %,
Temperature 40.0 °C
 1150 psi

@Strain 6.00 %,
Temperature 104 °F
 ISO 11403-1 -2
7.94 MPa

@Strain 100.62 %,
Temperature 120 °C
 1150 psi

@Strain 100.62 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.12 MPa

@Strain 17.37 %,
Temperature 90.0 °C
 1180 psi

@Strain 17.37 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.29 MPa

@Strain 120.67 %,
Temperature 120 °C
 1200 psi

@Strain 120.67 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.30 MPa

@Strain 27.5 %,
Temperature 100 °C
 1200 psi

@Strain 27.5 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.45 MPa

@Strain 6.00 %,
Temperature 23.0 °C
 1230 psi

@Strain 6.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
8.55 MPa

@Strain 133.56 %,
Temperature 120 °C
 1240 psi

@Strain 133.56 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.61 MPa

@Strain 37.5 %,
Temperature 100 °C
 1250 psi

@Strain 37.5 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.73 MPa

@Strain 7.83 %,
Temperature 40.0 °C
 1270 psi

@Strain 7.83 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
8.77 MPa

@Strain 48.22 %,
Temperature 100 °C
 1270 psi

@Strain 48.22 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.92 MPa

@Strain 150.03 %,
Temperature 120 °C
 1290 psi

@Strain 150.03 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.94 MPa

@Strain 61.79 %,
Temperature 100 °C
 1300 psi

@Strain 61.79 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.00 MPa

@Strain 27.59 %,
Temperature 90.0 °C
 1310 psi

@Strain 27.59 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.12 MPa

@Strain 75.36 %,
Temperature 100 °C
 1320 psi

@Strain 75.36 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.15 MPa

@Strain 24.0 %,
Temperature 90.0 °C
 1330 psi

@Strain 24.0 %,
Temperature 194 °F
 ISO 11403-1 -2
9.33 MPa

@Strain 88.94 %,
Temperature 100 °C
 1350 psi

@Strain 88.94 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.36 MPa

@Strain 37.81 %,
Temperature 90.0 °C
 1360 psi

@Strain 37.81 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.54 MPa

@Strain 173.66 %,
Temperature 120 °C
 1380 psi

@Strain 173.66 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.57 MPa

@Strain 102.51 %,
Temperature 100 °C
 1390 psi

@Strain 102.51 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.57 MPa

@Strain 48.04 %,
Temperature 90.0 °C
 1390 psi

@Strain 48.04 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.78 MPa

@Strain 61.66 %,
Temperature 90.0 °C
 1420 psi

@Strain 61.66 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.78 MPa

@Strain 42.0 %,
Temperature 90.0 °C
 1420 psi

@Strain 42.0 %,
Temperature 194 °F
 ISO 11403-1 -2
9.98 MPa

@Strain 122.51 %,
Temperature 100 °C
 1450 psi

@Strain 122.51 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.02 MPa

@Strain 75.29 %,
Temperature 90.0 °C
 1453 psi

@Strain 75.29 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.07 MPa

@Strain 17.86 %,
Temperature 60.0 °C
 1461 psi

@Strain 17.86 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
10.26 MPa

@Strain 88.92 %,
Temperature 90.0 °C
 1488 psi

@Strain 88.92 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.29 MPa

@Strain 136.08 %,
Temperature 100 °C
 1492 psi

@Strain 136.08 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.31 MPa

@Strain 200.16 %,
Temperature 120 °C
 1495 psi

@Strain 200.16 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
10.54 MPa

@Strain 102.54 %,
Temperature 90.0 °C
 1529 psi

@Strain 102.54 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.71 MPa

@Strain 153.23 %,
Temperature 100 °C
 1553 psi

@Strain 153.23 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.74 MPa

@Strain 8.21 %,
Temperature 23.0 °C
 1558 psi

@Strain 8.21 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2