SCG Chemicals EL-Leneâ„¢ H5211PC High Density Polyethylene Pipe Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer	SCG Chemicals Co.
Trade Name	EL-Lene™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SCG Chemicals EL-Leneâ„¢ H5211PC High Density Polyethylene Pipe Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Characteristics: Good processing, high thermal stability, good balance of MRS, SCG, and RCPRecommended Applications: Water pressure and gas pipesCertification: Certified by EXOVA, LNE, AENOR, INSTA, GOSTInformation provided by SCG Chemicals

Physical Properties	Metric	English	Comments
Specific Gravity	0.959 g/cc	0.959 g/cc	ISO 1183
Environmental Stress Crack Resistance	>= 10000 hour	>= 10000 hour	F0; ASTM D1693
Oxidative Induction Time (OIT)	>= 70 min @Temperature 200 Â°C	>= 70 min @Temperature 392 Â°F	ISO/TR10837
Carbon Black Loading	2.3 %	2.3 %	ISO 6964
Melt Flow	0.40 g/10 min @Load 5.00 kg, Temperature 190 Â°C	0.40 g/10 min @Load 11.0 lb, Temperature 374 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	62	62	ASTM D2240
Tensile Strength at Break	33.0 MPa	4790 psi	Crosshead speed 100 mm/min; ISO 527
Tensile Strength, Yield	22.0 MPa	3190 psi	Crosshead speed 100 mm/min; ISO 527
Elongation at Break	812 %	812 %	Crosshead speed 100 mm/min; ISO 527
Flexural Modulus	1.00 GPa	145 ksi	ASTM D790
Izod Impact, Notched	0.745 J/cm @Temperature -20.0 Â°C	1.40 ft-lb/in @Temperature -4.00 Â°F	ASTM D256
	1.57 J/cm @Temperature 0.000 Â°C	2.94 ft-lb/in @Temperature 32.0 Â°F	ASTM D256
	2.60 J/cm @Temperature 23.0 Â°C	4.87 ft-lb/in @Temperature 73.4 Â°F	ASTM D256
Hydrostatic Design Basis	8.00 MPa	1160 psi	ISO 9080

Thermal Properties	Metric	English	Comments
Brittleness Temperature	<= -60.0 Â°C	<= -76.0 Â°F	ASTM D746

Descriptive Properties	Value	Comments
Carbon Black/Pigment Dispersion (grade)	<3	ISO 18553
Color	Black
Rapid Crack Propagation	>8 bar	ISO 13477
Resistance to Gas Constituents	>20 hours	ISO 1167
Resistance to Slow Crack Growth	>500 hours	ISO 13479