Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM XH2315 TPI Resin Extem XH2315 Resin |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM XH2315 TPI Resin (Asia Pacific) Extem XH2315 Resin |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM XH2315 TPI Resin (Europe-Africa-Middle East) Extem XH2315 Resin |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP IFL36R PA6.12 (Europe-Africa-Middle East) Internally lubricated PA6.12, containing Glass Fiber and PTFE |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | DAM; ISO 527 Type 1 A |
Solvay Technyl® A 60G1 V25 25% Glass Reinforced Nylon 66, Flame Retardant This Red Phosphorous and Halogen free flame retardant grade, combines excellent all-round mechanical properties with outstanding flame retardancy (UL 5VA at 1.6mm) and electrical performance. This p.. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP OFL38A PPS - Branched (Europe-Africa-Middle East) LNP* LUBRICOMP* OFL38A is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features include : Internally Lubricated. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ISO 527 Type 1A |
Solvay TECHNYLSTARâ„¢ S 60G1 V30 PA6, 30% glass filled, DRY Description: TECHNYLSTARâ„¢ S 60G1 V30 is a reinforced 30% GF organophosphorous flame retarded grade based on a patented high flow polyamide 6 resin (TechnylStar). This product is heat stabilized.. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP KF006 Acetal Copoly LNP* THERMOCOMP* KF006 is a compound based on Acetal Copolymer resin containing 30% Glass Fiber. Added features of this material include: Chemically Coupled. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP LF004E PEEK LNP* THERMOCOMP* LF004E is a compound based on Polyetheretherketone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon DE0049 PC (Europe-Africa-Middle East) LNP* Stat-kon* DC-1004 FR is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.This.. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp RFB24 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RFB24 is a compound based on PA 66 resin containing Glass Bead, Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOTUF PX06417 PA 6 LNP THERMOTUF* PX06417 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | DAM; ISO 527 Type 1 A |
Solvay Technyl Starâ„¢ S 60G1 V30 30% Glass Reinforced Nylon 6, Flame Retardant This Halogen free flame retardant grade, based on high fluidity Technyl Star, combines excellent all-round mechanical properties with outstanding flame retardancy and electrical performance. This pr.. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ISO 527-2 |
Tisan TISLAMID® 66 20% Glass Fiber Reinforced Nylon 66 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
Toyobo VYLOPET® EMC330 Injection Molding Polyester Resin, Hydrolysis Resistant Applications: Electric rice cooker partsBathroom appliancesFeatures: Good hydrolysis resistanceInformation provided by Toyobo. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
Eurostar Staramide RFB24 PA66, 20/10% Glass Fiber/Glass Bead Filled Injection Molded RFB24 is a Glass Bead and Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as Staramide 66 2010VK Z3)Information provided by Polymer Technology & Services, the North American.. |