Tisan TISLAMID® 66 20% Glass Fiber Reinforced Nylon 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer	Tisan Engineering Plastics
Trade Name	TISLAMID®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Tisan TISLAMID® 66 20% Glass Fiber Reinforced Nylon 66.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElectric isolationEasy processabilityHigh mechanical resistanceExcellent flame retardanceHigh moisture absorptionExcellent temperature resistanceHigh performance / affordable priceAbrasion resistanceTISLAMID has an excellent resistance to weak alkalis and organic solvents. It has a good resistance to weak acids, alcohols, hydrocarbons, and engine fuels. It has a medium resistance to strong alkalis and a weak resistance to strong acids.

Physical Properties	Metric	English	Comments
Density	1.28 g/cc	0.0462 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in
Ash	20 %	20 %	ISO 3451

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	85	85	ISO 868
Tensile Strength at Break	147 MPa	21300 psi	ISO 527-2
Tensile Strength, Yield	150 MPa	21800 psi	ISO 527-2
Elongation at Break	3.0 %	3.0 %	ISO 527-2
Elongation at Yield	3.0 %	3.0 %	ISO 527-2
Modulus of Elasticity	6.50 GPa	943 ksi	ISO 527-2
Izod Impact, Notched (ISO)	8.00 kJ/m²	3.81 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
Melting Point	260 - 265 °C	500 - 509 °F
Vicat Softening Point	255 °C	491 °F	ISO 306
Heat Distortion Temperature	260 °C	500 °F	ISO 75-2
Flammability, UL94	HB	HB
Glow Wire Test	650 °C	1200 °F	60695-2-10

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	500 V	500 V	TS EN 60112

Processing Properties	Metric	English	Comments
Feed Temperature	70.0 - 90.0 °C	158 - 194 °F
Rear Barrel Temperature	260 - 280 °C	500 - 536 °F	Aft-1. Region Temperature
Middle Barrel Temperature	260 - 280 °C	500 - 536 °F	Mid-2. Region Temperature
Front Barrel Temperature	260 - 280 °C	500 - 536 °F	Pre-3. Region Temperature
Nozzle Temperature	250 - 270 °C	482 - 518 °F
Melt Temperature	260 - 290 °C	500 - 554 °F
Drying Temperature	90.0 - 100 °C	194 - 212 °F	Predrying Temperature
Dry Time	3 - 4 hour	3 - 4 hour	Predrying Time
Moisture Content	2.1 %	2.1 %	ISO 62

Descriptive Properties	Value	Comments
Block Temperature	75-85°C