Eurostar Staramide RFB24 PA66, 20/10% Glass Fiber/Glass Bead Filled Injection Molded

Category Ceramic , Machinable Ceramic , Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide RFB24 PA66, 20/10% Glass Fiber/Glass Bead Filled Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RFB24 is a Glass Bead and Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as Staramide 66 2010VK Z3)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 1.2 %

@Temperature 23.0 °C,
Time 86400 sec
1.2 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62-1
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
on Tensile Bar; ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 147 MPa
21300 psi
5 mm/min; ISO 527
Elongation at Break 3.4 %
3.4 %
5 mm/min; ISO 527
Tensile Modulus 7.80 GPa
1130 ksi
1 mm/min; ISO 527
Flexural Strength 213 MPa
30900 psi
2 mm/min; ISO 178
Flexural Yield Strength 215 MPa
31200 psi
2 mm/min; ISO 178
Flexural Modulus 6.50 GPa
943 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
19.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 101 µm/m-°C

@Temperature 23.0 - 60.0 °C
56.1 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 257 °C
495 °F
Flatw 120x10x4, sp=64 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 238 °C
460 °F
Flatw 120x10x4, sp=64 mm; ISO 75/Af
Processing Properties Metric English Comments
Rear Barrel Temperature 265 - 280 °C
509 - 536 °F
Zone 1
Middle Barrel Temperature 270 - 285 °C
518 - 545 °F
Zone 2
Front Barrel Temperature 270 - 285 °C
518 - 545 °F
Zone 3
Melt Temperature 270 - 285 °C
518 - 545 °F
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.20 %
0.20 %