Polymer Property : Tensile Strength at Break = 11600 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | STN EN ISO 527-2 |
| Plastcom SLOVAMID 66 W 40 Polyamide 66, 40% Mineral Filled FeaturesPA 66 with the content of 40% chemically modified mineral filler. Used for grips of electric hand tools, hobby tools, gear wheels, covers of electric tools, flat products, automobile wheel .. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
| Nilit FRIANYL B63 F Raw extruded nylon 6 for injection molding Raw extruded nylon 6 for injection molding, highly crystallized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
| Nilit FRIANYL B63 KV30 Nylon 6 for injection molding, 30% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp DFP22H PC LNP* Lubricomp* DFP22H is a compound based on Polycarbonate containing Glass Fiber and PTFE. Characteristics of this grade are: Internally Lubricated and Healthcare.This data was supplied by SABIC.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
| Nilit FRIANYL B63 H Nylon 6 for injection molding Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Molded; ASTM D882 |
| Honeywell Aegisâ„¢ H135MP Nylon 6 Extrusion Grade Homopolymer Film Description: Aegis H135MP is a lubricated and nucleated high viscosity, nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21 CFR.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Conditioned; ISO 527-1/-2 |
| Lanxess Durethan® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, higher impact and notched impact strength and also higher energy absorption under biaxial impact load than BKV 130, conditioning .. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-1/-2 |
| Lanxess Pocan® B 3215 XF 000000 PBT, 10% Glass Fiber PBT, 10% glass fibers, injection molding, improved flowability, impact modified |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 4012G PBT (Europe-Africa-Middle East) VALOX 4012G is a 10% glass fibre reinforced PBT injection moulding resin with excellent mechanical properties. Applications: connectors. This grade is a 4012 with improved cycle time and ductility. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp 9X06477 SPS LNP* Thermocomp* 9X06477 is a compound based on Syndiotactic Polystyrene resin containing Glass Fiber. Characteristics of this grade is Heat Stabilized.This data was supplied by SABIC-IP for the Am.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GFN2 PPE+HIPS (Europe-Africa-Middle East) NORYL GFN2 is a standard 20 % glass fibre reinforced material with a HDT/A of 130C according ISO 75. NORYL GFN2 can be used for all applications where a higher modulus is required. NORYL GFN2 is ava.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP RB004 PA 66 LNP* THERMOCOMP* RB004 is a compound based on Nylon 66 containing Glass Beads. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp ZF0041XC PPE+PS (Europe-Africa-Middle East) LNP* THERMOCOMP* ZF0041XC is a compound based on PPE+PS Blend resin containing Glass Fiber and Flame retardant. Added features include Flame Retardant.This data was supplied by SABIC-IP for the Euro.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL GTX GTX8408 PPE+PA Noryl GTX* GTX8408 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is glass filled and suitable for injection molding. The elongation of this material is higher than GTX8410W.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-93 |
| Wellman Wellamid® T512-BK 15% Talc/Glass Reinforced, Dimensionally Stable Grade Nylon 6 Description: Talc/Glass Reinforced, Dimensionally Stable Grade Nylon 6Information provided by Wellman. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D638 |
| A. Schulman SCHULAMID® 66 MK30HI 30% Mineral Reinforced, Impact Modified Nylon 66 Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® BG-30 EC PA6-GF30 Information provided by EMS Grivory |
|||
| Tensile Strength at Break | 80.0 MPa @Temperature 23.0 °C |
11600 psi @Temperature 73.4 °F |
DAM; ISO 527 |
| DuPont Performance Polymers Zytel® FR7025V0F NC010 Nylon 66
(Unverified Data**) Zytel® FR7025V0F NC010 is a flame retardant polyamide 66 resin for injection molding. It does not contain elemental phosphorous, halogens or heavy metals.Information provided by DuPont Performance.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| Eurostar Staramide R1000K PA66, Injection Molded Staramide R1000K is an Unreinforced Radiation Crosslinkable Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
| Tensile Strength at Break | 80.0 MPa @Temperature -40.0 °C |
11600 psi @Temperature -40.0 °F |
ASTM Test |
| BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
| Tensile Strength at Break | 80.0 MPa @Temperature -40.0 °C |
11600 psi @Temperature -40.0 °F |
ISO Data |
| BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | TD |
| BASF Ultramid® C33 LN 0.025 mm Blown Film PA6/66 Description: Ultramid® C33 LN is a copolyamide 6/66 grade of intermediate viscosity for the production of mulitlayer film. Its lower melting point than standard PA 6 is advantageous for coextrusion.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D638 |
| Aclo Accutech Nylon 6 NY0730G10L Glass Reinforced |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO R 527 |
| Addiplast Addinyl A2 ZG30 Nylon 66, 30% Glass Bead Glass bead reinforced, improved stiffness and dimensional stability, increased thermal aging stabilityInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 80.0 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec |
11600 psi @Temperature 320 - 347 °F, Time 5000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
| Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Dry, 20% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 0.2 in/min; ASTM Test |
| BASF Ultramid® C33 01 PA66/6 (Dry) Ultramid C33 01 is an intermediate viscosity PA6/66 grade. Its lower melting point than standard PA6 is advantageous for coextrusion with temperature sensitive polymers like EVOH. It conforms to F.. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Conditioned; ISO R 527 |
| Addiplast Addinyl C2 ZV20 Nylon 66/6, 20% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-1/-2 |
| Lanxess Durethan® DP 2801 000000 Nylon 66 PA 66 injection molding grade, non-reinforced, UL 94V-2 off 0,75 mm (listed), GWFI: 960°C off 0.75 mm, GWIT: 775°C off 0,75 mm, halogen-free |
|||