SABIC Innovative Plastics NORYL GTX GTX8408 PPE+PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX8408 PPE+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX* GTX8408 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is glass filled and suitable for injection molding. The elongation of this material is higher than GTX8410W. The glass content enables the material to be used in structural applications and electrical connectors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.350 % | 0.350 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 26.3 g/10 min @Load 5.00 kg, Temperature 280 °C |
26.3 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 22 g/10 min @Load 5.00 kg, Temperature 280 °C |
22 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
| 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527 |
| 10.2 % | 10.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.3 % | 4.3 % | Type I, 5 mm/min; ASTM D638 |
| 4.5 % | 4.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.56 GPa | 516 ksi | 5 mm/min; ASTM D638 |
| 4.00 GPa | 580 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 133 MPa | 19300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.32 GPa | 482 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.52 GPa | 511 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D256 |
| 0.450 J/cm @Temperature -30.0 °C |
0.843 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 84.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 84.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 239 °C @Thickness 3.20 mm |
462 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 224 °C | 435 °F | Rate B/50; ASTM D1525 |
| 224 °C | 435 °F | Rate B/50; ISO 306 | |
| 224 °C | 435 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- NOVA Chemicals Dylark® 432 High-Heat Styrenic Copolymer
- PolyOne OnColor™ 30BKA488 Black Polyvinyl Chloride, Unspecified (PVC, Unspecified)
- Seals Eastern Perflas® 9294 Perfluorinated Rubber
- Samsung Cheil Industries Starex® NH-0825 ABS, Unreinforced FR
- A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Total PPR 7860 Controlled Rheology Grade Propylene Copolymer for Spunbond Nonwoven Fabrics, Multifilament Yarns and Extrusion Coating
- Dow Corning SYL-OFF® PMCP7689 Crosslinker
- DuPont Teijin Films Mylar® P25T Polyester Film, 75 Gauge
- AK Steel ZINCGRIP® GA Hot Dip Galvannealed Carbon Steel, Dent Resistant (DR 180)
- Lucobit Lucolit® 1310 Polyolefin TPO Granules, Grey
Copyright © lookpolymers.com All Rights Reserved