Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® DP 2801 000000 Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66 injection molding grade, non-reinforced, UL 94V-2 off 0,75 mm (listed), GWFI: 960°C off 0.75 mm, GWIT: 775°C off 0,75 mm, halogen-free
Physical Properties Metric English Comments
Density 1.143 g/cc
0.04129 lb/in³
ISO 1183
Viscosity Test 133 cm³/g
133 cm³/g
Viscosity number; ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow 0.00114 cm/cm
0.00114 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.00122 cm/cm
0.00122 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Conditioned; ISO 527-1/-2
80.0 MPa
11600 psi
ISO 527-1/-2
Tensile Strength, Yield 55.0 MPa
7980 psi
Conditioned; ISO 527-1/-2
94.0 MPa
13600 psi
ISO 527-1/-2
Elongation at Break 10 %
10 %
Nominal; ISO 527-1/-2
11 %
11 %
ISO 527-1/-2
155 %
155 %
Nominal, Conditioned; ISO 527-1/-2
230 %
230 %
Conditioned; ISO 527-1/-2
Elongation at Yield 4.2 %
4.2 %
ISO 527-1/-2
20 %
20 %
Conditioned; ISO 527-1/-2
Tensile Modulus 1.40 GPa
203 ksi
Conditioned; ISO 527-1/-2
3.50 GPa
508 ksi
ISO 527-1/-2
Charpy Impact Unnotched 11.0 J/cm²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
12.0 J/cm²

@Temperature -30.0 °C
57.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
18.5 J/cm²

@Temperature -30.0 °C
88.0 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Conditioned; ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eA
Impact 3730
3730
Puncture maximum force (N); ISO 6603-2
4630
4630
Puncture maximum force, Conditioned (N); ISO 6603-2
2396

@Temperature -30.0 °C
2396

@Temperature -22.0 °F
Puncture maximum force (N); ISO 6603-2
Puncture Energy 13.1 J
9.66 ft-lb
ISO 6603-2
27.2 J
20.1 ft-lb
Conditioned; ISO 6603-2
5.10 J

@Temperature -30.0 °C
3.76 ft-lb

@Temperature -22.0 °F
ISO 6603-2
5.10 J

@Temperature -30.0 °C
3.76 ft-lb

@Temperature -22.0 °F
Conditioned; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C
38.9 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
Melting Point 265 °C
509 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 60.0 °C
140 °F
ISO 75-1/-2
Flammability, UL94 V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
IEC 60695-11-10
Oxygen Index 30 %
30 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Additives Flame retarding agent
Features Flame retardant
Form Pellets
ISO Shortname ISO 1874-PA 66,MF,14-030; ISO 1043-PA FR(30)
Processing Injection molding