- Polymer Property : Tensile Strength at Break = 89.0 MPa
Polymer Property : Tensile Strength at Break = 89.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFP34 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Silicone. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL34H PC LNP LUBRICOMP* DFL34H is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Healthcare. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DX00714H PC LNP LUBRICOMP* DX00714H is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Wear Resistant, Healthcare. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES LNP LUBRICOMP* JFL36 is a compound based on Polyethersulfone resin containing 30% Glass Fiber, 15% PTFE. Added featurs of this material is: Wear Resistant. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Asia Pacific) LNP LUBRICOMP* JFL36 is a compound based on Polyethersulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RAL23 PA 66 LNP LUBRICOMP* RAL23 is a compound based on Nylon 66 resin containing 15% PTFE, 10% Aramid Fiber. Added features of this material include: Wear Resistant. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RAL23 PA 66 (Asia Pacific) LNP LUBRICOMP* RAL23 is a compound based on Nylon 66 resin containing Aramid Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RAL23S PA 66 LNP LUBRICOMP* RAL23S is a compound based on Nylon 66 resin containing 10% PTFE, 15% Aramid. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RAL23S PA 66 (Asia Pacific) LNP LUBRICOMP* RAL23S is a compound based on Nylon 66 resin containing Aramid Fiber, PTFE. Added features of this material include: Heat Stabilized. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RAL23S PA 66 (Europe-Africa-Middle East) LNP LUBRICOMP* RAL23S is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Heat Stabilized. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM 8015 PEI High flow Polyetherimide blend. Meets FAR 25.853 and OSU 100/100 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM 8015 PEI (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 100/100 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 815 PBT 15% GR PBT+ PET, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 855 PBT 15% GR PBTP, UL94 V-0 rated. Improved surface appearance. For external housings: steam irons, appliance housings and lighting parts. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 855 PBT (Asia Pacific) 15% GR PBTP, UL94 V-0 rated. Improved surface appearance. For external housings: steam irons, appliance housings and lighting parts. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 (Asia Pacific) LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Asia Pacific) Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Europe-Africa-Middle East) Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS (Asia Pacific) Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS (Europe-Africa-Middle East) Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ISO 527-2 |
| Tisan TISOPLEN® 30% Glass Fiber Reinforced Heat Stabilized Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D638 |
| Beijing Chemical Industry KAIFA® HN201-G10 PA6 Resin 10% glass fiber reinforcedInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | GB/T 1040 |
| Beijing Evergrow Resources MC Nylon Information provided by Beijing Evergrow Resources. |
|||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® K4530 PBT 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||