SABIC Innovative Plastics LNP LUBRICOMP DX00714H PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DX00714H PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* DX00714H is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Wear Resistant, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D638 |
| 90.0 MPa | 13100 psi | ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| 3.3 % | 3.3 % | ISO 527 | |
| Tensile Modulus | 6.34 GPa | 920 ksi | 1 mm/min; ISO 527 |
| 6.55 GPa | 950 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| 137 MPa | 19900 psi | ASTM D790 | |
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO 178 |
| 5.31 GPa | 770 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.36 J/cm | 6.29 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 30.0 J | 22.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 72.0 J | 53.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.51 | 0.51 | ASTM D3702 Modified |
| K (wear) Factor | 888 x 10-8 mm³/N-M | 441 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 71.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- ExxonMobil LD 102.74 Thin Gauged Film Resin (discontinued **)
- Ineos ABS Lustran® SAN 51
- Henkel Hysol EA 9696 Film Adhesive
- Sylvin Technologies 9925-65 Natural PVC Molding Compound
- SABIC Innovative Plastics LNP Stat-kon TE002
- M Cubed Technologies RBBC-751 Reaction Bonded Boron Carbide
- Polyram PlusTek RA301G6 Nylon 6.6, 30% Glass Fiber
- BASF Heligoen® Green L 9361 Color Additive
- Reade Advanced Materials Wollastonite (CaSiO3 or CaO.SiO2)
- BASF Ultramid® B3WG6 BK00564 BGVW 30% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved