SABIC Innovative Plastics LNP LUBRICOMP RAL23 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RAL23 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RAL23 is a compound based on Nylon 66 resin containing 15% PTFE, 10% Aramid Fiber. Added features of this material include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.017 - 0.018 cm/cm @Time 86400 sec |
0.017 - 0.018 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.021 cm/cm @Time 86400 sec |
0.020 - 0.021 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 |
| 89.0 MPa | 12900 psi | ASTM D638 | |
| Elongation at Break | 5.9 % | 5.9 % | ASTM D638 |
| 6.3 % | 6.3 % | ISO 527 | |
| Tensile Modulus | 3.68 GPa | 534 ksi | 50 mm/min; ASTM D638 |
| 3.80 GPa | 551 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 107 MPa | 15500 psi | ISO 178 |
| 131 MPa | 19000 psi | ASTM D790 | |
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| 3.93 GPa | 570 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.460 J/cm | 0.862 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.38 | 0.38 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.32 | 0.32 | ASTM D3702 Modified |
| K (wear) Factor | 46.3 x 10-8 mm³/N-M | 23.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 97.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 98.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 171 °C @Thickness 3.20 mm |
340 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Overview of materials for Polyphthalamide (PPA)
- Abatron AboCast 50-3/AboCure 8012-7 Epoxy (discontinued **)
- Fiberfil® PP-61/CC/40 Polypropylene Copolymer, 40% Calcium Carbonate
- Global PP-2340-TC Polypropylene Block Copolymer
- Teknor Apex Telcar® TL-2363A Thermoplastic Elastomer
- Wellman Wellamid® 22L-N Unfilled Nylon 66, Lubricated
- Polyram RamShine PV111 Acrylonitrile Butadiene Styrene
- ChevronTexaco NLGI 1 Moly Grease EP
Copyright © lookpolymers.com All Rights Reserved