SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D 792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0066 cm/cm @Time 86400 sec |
0.0066 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ISO 294 |
| 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D 638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D 638 |
| Elongation at Break | 22 % | 22 % | ASTM D 638 |
| Tensile Modulus | 6.71 GPa | 973 ksi | 1 mm/min; ISO 527 |
| 10.34 GPa | 1500 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D 790 |
| 138 MPa | 20000 psi | ISO 178 | |
| Flexural Modulus | 4.82 GPa | 699 ksi | ASTM D 790 |
| 5.30 GPa | 769 ksi | ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.84 J/cm @Temperature 23.0 °C |
7.19 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 47.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Polyplastic Armamid® PA GF25-1FR Nylon 6, 25% Glass Fiber
- NOVA Chemicals Novapol® TI-0338-A MDPE Masterbatch Resin
- Polimeri Europa KOBLEND PCA PD 55 PC+ABS (discontinued **)
- Solvay Specialty Polymers Polymist® XPP 515-S Polytetrafluoroethylene (PTFE)
- Sharadaa Ceramics REFINSUL 11LI Insulating Castables Medium/High Purity
- A. Schulman POLYBATCH™ Mahogany 50381 Concentrate Based in Polyethylene
- A. Schulman POLYFORT™ FPP 3452 Mineral Filled Copolymer Polypropylene
- ExxonMobil Enmist EP 320
- ExxonMobil Enable™ 20-10CH Metallocene Polyethylene Resin (Africa & Middle East Grade)
Copyright © lookpolymers.com All Rights Reserved