SABIC Innovative Plastics ULTEM 8015 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 8015 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Polyetherimide blend. Meets FAR 25.853 and OSU 100/100 with low toxicity, smoke, and flame evolution. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 2.7 g/10 min @Load 6.60 kg, Temperature 295 °C |
2.7 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 80 % | 80 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.30 GPa | 479 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 144 MPa | 20900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| 20.82 J/cm @Thickness 3.20 mm |
39.00 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Dart Drop, Total Energy | 71.0 J | 52.4 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 56.0 J @Temperature -30.0 °C |
41.3 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C @Thickness 6.40 mm |
369 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| OSU total heat release (2 minute test) | 45kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 80kW/m^2 | FAR 25.853 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, 120 E-Glass Reinforced
- SABIC Innovative Plastics Lexan® HP4R PC
- Shakespeare FN-29 Freshwater Nylon Copolymer Fishing Line, 100 lb
- Techmer ES HiFill® PA6/6 GF30 L 30% Glass Filled
- Destech Silicon Carbide, Solid or Foamed
- ExxonMobil Escorene™ LD 706.15 Cast Ethylene Vinyl Acetate Copolymer
- Dow TUFLIN™ HSE-1003 NT 7 Linear Low Density Polyethylene Resin
- M. Holland Company MAGMA® LL1091-AS LLDPE (discontinued **)
- Parker Chomerics CHO-BOND 1053, Part A Conductive Powder
- Cosmic Plastics D44 Mineral Filled Ortho Diallyl Phthalate Molding Compound
Copyright © lookpolymers.com All Rights Reserved