- Polymer Property : Tensile Strength at Break = 75.0 MPa
Polymer Property : Tensile Strength at Break = 75.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | |
| Plastcom SLOVALEN PC 79 GF 20 PP, 20% glass fibre, mod. of mech. prop. FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 20% glass fibre, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP... |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | STN EN ISO 527-2 |
| Plastcom SLOVAMID 6 FRC 2 LS Polyamide 6, Halogen Free Flame Retardant, Light Stabilization FeaturesLongterm external use is possible because of the material stabilization with the light stabilizers on the HALS basis. Meets the flammability in accordance with the norm DIN 4102 - B1. PA 6.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | |
| Plastcom SLOVAMID 6 FRM 1 PA6, flame retardant FeaturesDetermined for electrotechnical use. Delivered in natural mode. PA 6 for injection moulding with reduced flammability, with nonhalogen flame retardant. Excellent fluidity of the material pre.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Nilit FRIANYL A63 HH-KV20 Nylon 6.6 for injection molding, 20% glass ball reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | <= 75.0 MPa | <= 10900 psi | ISO/R527 |
| Polykemi AB SCANAMID 66 A12^ X30 Nylon 66, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | <= 75.0 MPa | <= 10900 psi | ISO/R527 |
| Polykemi AB SCANMID 6 B12^ F Nylon 6 Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HP6NR PC (Asia Pacific) Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ASTM D638 |
| LG Chemical IH830C PMMA, General Purpose Grade for Injection Molding Highest of all grades in heat resistanceMechanical strength and surface hardnessParticularly recommended for tail lamp, reflectors, and general lighting fixturesFeatures: Excellent transparency and .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| GEHR Plastics PA 6.6-30GF Nylon 6.6, 30% Glass Fiber, Conditioned |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Conditioned; ISO 527-1/-2 |
| Lanxess Durethan® BKV 15 000000 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Sample Type 1B, 50mm/min; ISO 527-1/2:1993 |
| Global EPP PA 612 Copolymer Cast Polyamide 612 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 Type 1A |
| Solvay TECHNYL® A 222 Black 1N PA66, DRY Description: Unreinforced polyamide PA66, medium viscosity, heat stabilized, for injection molding, fast crystallization, for short cycles .Available in: EuropeProduct Applications: TECHNYL A 222 of.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 Type 1A |
| Solvay TECHNYL® B 216 Natural D PA66/6, DRY Description: Unreinforced copolyamide 66/6, medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL B 216 offers an excellent combination between impact resistance,.. |
|||
| Tensile Strength at Break | 75.0 MPa @Temperature 80.0 °C |
10900 psi @Temperature 176 °F |
50 mm/min, 1A; ISO 527 |
| SABIC Innovative Plastics SABIC STAMAX 40YM240 PP SABIC® STAMAX 40YM240 is a 40% long glass fiber reinforced polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 16497161... |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM 4001 PEI (Europe-Africa-Middle East) PTFE filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM UF5011S PEI Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Valox® 701 PBT (Asia Pacific) 35% glass/mineral alloy, excellent electrical performance to dielectric breakdown. Developed for automotive distributor caps.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL NH7111E PPE+HIPS (Asia Pacific) Noryl* EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR a.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-93 |
| Wellman Wellamid® 42L-N Nylon 6, General Purpose All information provided by Wellman Engineered Resins. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® BG-15 S PA6-GF15 Product description: Grilon BG-15 S is a heat stabilized PA6 injection molding grade with 15% glass fibers. Grilon BG-15 S has the following important properties: Excellent surface finishEasy flowin.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| Chi Mei Kibisan® PN-127 SAN Heat Resistant |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50%RH; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66
(Unverified Data**) 13% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G13HS1L BK031 is a 13% glass fiber reinforced heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Eurotec® Tecomid® NA40 MR15 NL IL PA 6.6 15% mineral reinforced, impact modified Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
| Tensile Strength at Break | 75.0 MPa @Temperature 80.0 °C |
10900 psi @Temperature 176 °F |
ISO Data |
| BASF Petra® 130 FR BK-112 30% Glass Filled PET Petra 130 FR BK-112 is a 30% glass fiber reinforced, black pigmented, flame retardant injection molding compound based on post-consumer and post-industrial recycle polyethylene erephthalate feedstoc.. |
|||
| Tensile Strength at Break | 75.0 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec |
10900 psi @Temperature 266 - 302 °F, Time 20000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
| Akro-Plastic Akromid® B3 GF 20 (2470) PA 6 Dry, 20% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | TD |
| BASF Ultramid® B36 LN 0.04 mm Cast Film Cold Chillroll Product comes in 2-2.5 mm round pellets.Information provided by BASF |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-1/-2 |
| BASF Ultramid® B3M6 Grey 22319 Q94 30% Mineral Filled PA6 (Dry) Description: 30% Mineral-filled injection molding grade for high impact industrial items having very high dimensional stability, such as automobile wheel covers.Information provided by BASF |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Grupo Repol Dinalon® B2S35 V2-7035 PA6 High Viscosity, V2 Halogen Free, RAL 7035 Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HPS6R PC (Europe-Africa-Middle East) Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam and gamma sterilizable... |
|||