SABIC Innovative Plastics SABIC STAMAX 40YM240 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC STAMAX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC STAMAX 40YM240 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® STAMAX 40YM240 is a 40% long glass fiber reinforced polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 16497161.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Filler Content | 40 % | 40 % | glass; ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 50 mm/min; ASTM D638 |
| 121 MPa | 17500 psi | 50 mm/min, 1A; ISO 527 | |
| 54.0 MPa @Temperature 120 °C |
7830 psi @Temperature 248 °F |
50 mm/min, 1A; ISO 527 | |
| 75.0 MPa @Temperature 80.0 °C |
10900 psi @Temperature 176 °F |
50 mm/min, 1A; ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 50 mm/min; ASTM D638 |
| 2.1 % | 2.1 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 8.30 GPa | 1200 ksi | 1 mm/min; ISO 527 |
| 8.47 GPa | 1230 ksi | 50 mm/min; ASTM D638 | |
| 4.50 GPa @Temperature 120 °C |
653 ksi @Temperature 248 °F |
1 mm/min; ISO 527 | |
| 5.70 GPa @Temperature 80.0 °C |
827 ksi @Temperature 176 °F |
1 mm/min; ISO 527 | |
| Flexural Modulus | 7.67 GPa | 1110 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.85 GPa | 1140 ksi | 2 mm/min, 64mm span; ISO 178 | |
| 5.55 GPa @Temperature 80.0 °C |
805 ksi @Temperature 176 °F |
2 mm/min, 64mm span; ISO 178 | |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 2.80 J/cm² @Temperature -30.0 °C |
13.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
ASTM D648 |
Users viewing this material also viewed the following:
- Quadrant EPP Proteus® LDPE - Low Density Polyethylene (ASTM Product Data Sheet)
- PolyOne Geon™ Vinyl Fittings 210(HS) Polyvinyl Chloride, Rigid (PVC, Rigid)
- Magyar Aluminum ALOLT 720 Aluminum Hydroxide
- Iran Petrochemical (PCC) I3S HC 7260(THE) High Density Polyethylene
- Hexion UP 802 Unsaturated Polyester Resin, High Surface Quality, Low Shrinkage, High Arc Resistance
- Teknor Apex Sinvicomp SHE 5200 Polyvinyl Chloride, Flexible
- Asahi Kasei Thermylene® P-40FG-0860 40% Glass Fiber Reinforced
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 84A
- Schott CONTURAX® Borosilicate Glass
Copyright © lookpolymers.com All Rights Reserved