SABIC Innovative Plastics ULTEM 4001 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 4001 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PTFE filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.600 % | 0.600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.1 % | 1.1 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 13 g/10 min @Load 5.00 kg, Temperature 360 °C |
13 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 130 MPa | 18900 psi | ISO 2039-1 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 30 % | 30 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 125 MPa | 18100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Limiting Pressure Velocity | 2.80 MPa-m/sec | 79900 psi-ft/min | 0.51 m/s; SABIC Method |
| Taber Abrasion, mg/1000 Cycles | 2.0 | 2.0 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature 23.0 - 150 °C |
21.7 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C @Temperature 23.0 - 150 °C |
22.2 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 208 °C | 406 °F | Rate B/50; ISO 306 |
| 210 °C | 410 °F | Rate B/120; ISO 306 | |
| 215 °C | 419 °F | Rate A/50; ISO 306 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Flammability, UL94 | V-1 @Thickness 1.60 mm |
V-1 @Thickness 0.0630 in |
UL 94 by SABIC-IP |
| 5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
UL 94 by SABIC-IP | |
| Oxygen Index | 48 % | 48 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Pacific Sintered Materials FN-253-T(HT) 4600 Powdered Metal
- Chevron Phillips HiD® 9706 HDPE Injection Molding Resin (discontinued **)
- Kazanorgsintez Cosintol-247
- Mallard Creek Polymers Tychem® 3100D Yield Modifier Additive
- SABIC Innovative Plastics NORYL GTX GTX6009 PPE+PS+PA6 (Asia Pacific)
- Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Tape Form
- Trelleborg Z500 Commercial SBR Rubber
- Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (3.5 mm Molded Thickness)
- ATI Allvac® Ti-17 Titanium Alloy, Heat Treatment: 899°C (1650°F) + Age
- A. Schulman ComAlloy Hiloy® 614 Nylon 6, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved