Grupo Repol Dinalon® B2S35 V2-7035 PA6 High Viscosity, V2 Halogen Free, RAL 7035
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® B2S35 V2-7035 PA6 High Viscosity, V2 Halogen Free, RAL 7035.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75/A |
| Vicat Softening Point | >= 200 °C | >= 392 °F | 50N; ISO 306 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Nye Lubricants 774VHF (NG) Synthetic Oil
- Network Polymers Softflex® 2701T Transparent
- DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound (d
- SABIC Innovative Plastics Lexan® HFD1910 PC Copolymer (Europe-Africa-Middle East)
- Karina Karintox ENCH./03 Polyolefin Compound
- Styrolution Terblend® S NM-31 ASA / PA
- Polyram Polytron P60B11 Homopolymer Polypropylene, Chemically Coupled 60% LGF
- CP-Polymer-Technik Wellamid® 6600/42 HWCP Nylon 66, Polymer Modified, Heat Stabilized, Dry
- Arlon 61089R040 0.040" (1.02 mm) Uncured/Cured Silicone Rubber with Denier Vectran HS Substrate
Copyright © lookpolymers.com All Rights Reserved