SABIC Innovative Plastics Valox® 701 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 701 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
35% glass/mineral alloy, excellent electrical performance to dielectric breakdown. Developed for automotive distributor caps.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D 792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 1.50 - 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0040 - 0.0060 cm/cm @Thickness 3.20 - 4.60 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0060 - 0.0090 cm/cm @Thickness 3.20 - 4.60 mm |
0.0060 - 0.0090 in/in @Thickness 0.126 - 0.181 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D 785 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 124 MPa | 18000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 5.51 GPa | 799 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C |
0.599 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.27 J/cm @Temperature 23.0 °C |
8.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 34.2 µm/m-°C @Temperature 60.0 - 138 °C |
19.0 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.70e+16 ohm-cm | 3.70e+16 ohm-cm | ASTM D 257 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
ASTM D 150 |
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
ASTM D 150 | |
| Dielectric Strength | 22.0 kV/mm @Thickness 3.20 mm |
559 kV/in @Thickness 0.126 in |
in air; ASTM D 149 |
| 25.5 kV/mm @Thickness 1.60 mm |
648 kV/in @Thickness 0.0630 in |
in oil; ASTM D 149 | |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
ASTM D 150 |
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
ASTM D 150 |
Users viewing this material also viewed the following:
- Formosa Plastics Formolene® HP5221 Pipe HDPE (discontinued **)
- IRPC Polimaxx Polene 2346S Polypropylene Block Copolymer
- Multibase Multi-Flex® TPE A 6221 HR BLK
- Saint-Gobain CHR® M815 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics Valox® SHF4340 PBT
- Suzhou Hipro Polymers Hiprolon® 90 NN Nylon 612, dry
- Master Bond X17 Elastomer Based One Component Adhesive and Primer
- Beijing Ranger Chem 6690-3 Liquid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved