Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Europe-Africa-Middle East) Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol.. |
|||
Tensile Strength at Break | 50.0 - 65.0 MPa | 7250 - 9430 psi | ASTM D638-03 |
Proto3000 Objet Digital Materials™ DM_8320 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® BFL2000 PC (Asia Pacific) Non-Brominated, non-chlorinated flame retardant PC. Available in opaque white colors. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL1434 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1434 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade and is UV stabilized. This resin offers extreme low temperature (-40 C), exhibits exce.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® EXL1444 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1444 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade suitable for FDA compliant applications. This resin offers extreme low temperature (-.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXD173R PC (Europe-Africa-Middle East) LEXAN FXD173R is a UV stabilized translucent high flow grade for light diffusion special effects. The color package may affect performance. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML3042 PC (Europe-Africa-Middle East) LEXAN ML3042 offers an extremely low light transparency in combination with a very high reflection. This product is ideally suited for lighting reflectors. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DL003 PC LNP LUBRICOMP* DL003 is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® BFL2000U PC Lexan* BFL2000U Polycarbonat (PC) resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating. Lexan* BFL2000U is designed for hig.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50mm/min; ASTM D638 |
Kingfa JH950-402 Flame Retardant PC/ABS Alloy Features:UL V-0 @ 3.2mmExcellent balance propertiesHigh heat resistanceGood normal/low temperature impact strengthGood surfaceApplications:Small household appliance cabinetControllerSocketShell of a.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
IRPC Polimaxx Polene GA2850 High Density Polyethylene CHARACTERISTICS: HIGH MOLECULAR WEIGH FOR BLOW MOLDING GRADE, RIGID, STACKABLE AND HIGHLY SHOCK RESISTANT CONTAINERS, EXCELLENT IMPACT STRENGTH APPLICATIONS: BLOW MOLDING FOR L-RING DRUMS (200 LITRE.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
Lanxess Pocan® B 2505 000000 PBT PBT, non-reinforced, injection molding, flame retardant |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | |
LATI Latishield 36/AR-08A G/17-V0E ABS, Steel/Glass Fiber Reinforced, Flame Retardant EMI shielding product based on Acrylonitrile-Butadiene-Styrene copolymer (ABS). Steel fibers. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® IQ325 PBT (Asia Pacific) PBT resin, using chemically recycled post consumer PET Bottles. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® 5720U PBT+PC Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218 S40 Black 21 N PA66, 40% glass spheres, Conditioned Description: Polyamide 66, reinforced with 40% of glass spheres, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL ® A 218 S40 is used in all sectors of ind.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics XYLEX FXY330DF PC+POLYESTER Polyester+PC alloy. Diffusion Effect. Color package may affect performance. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 0.2 in/min; ASTM Test |
Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Dry) Terblend N NG-02 is a glass fibre reinforced ABS/PA6 blend with excellent dimensional stability, high impact strength and good surface appearance.Information provided by STYROLUTION, which is a join.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 216 S40 PA66, 40% glass spheres, Conditioned Description: Polyamide 66, reinforced with 40% of glass spheres, for injection molding.Available in: EuropeProduct Applications: TECHNYL ® A 216 S40 is used in all sectors of industry, offering a.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-93 |
Wellman Wellamid® XT1668-BK1 High Impact Nylon 66 Description: High Impact Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-1,-2 |
Covestro Bayblend® FR3040 PC/ABS Blend Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Injec.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® 2S 25 W 20 HL X nat PA610 Product Description: Grilamid 2S 25 W 20 HL X natural is a semi-flexible high viscosity heat and UV stabilized, impact modified and plasticized Polyamide 610, espcailly suitable for extrusion applic.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
Covestro Makrolon® SF800Z Polycarbonate, 5% Glass Filled MVR (300 °C/1.2 kg) 8.0 cm3/10 minStructural foam5 % Glass fiber reinforcedMilled fiberChlorine- and bromine-free flame retardantMedium viscosityEasy releaseInjection moldingAvailable in natural (o.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
Eurotec® Tecolen® CP10 GR15 NL PPCP, 15% glass fiber reinforced, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000 GS 30 HWCP 30% Glass Sphere Filled Nylon 6, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | DIN 53 455 |
Albis Plastics Tedur® L 9560 PPS, 50% Mineral High Gloss, Highest Surface Finish, Metallization w/o Base Coating. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Various High Temperature ReflectorsProcessing: Inje.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, Conditioned Availability:Asia PacificEuropeNorth AmericaAdditive:LubricantNucleating Agent Features: Fast Molding CycleGeneral PurposeGood Mold ReleaseGood StiffnessHigh RigidityLubricatedNucleatedUses:Bearings.. |
|||
Tensile Strength at Break | 50.0 MPa | 7250 psi | Transverse |
Goodfellow Carbon/Epoxy Composite Rod Carbon Fiber - Epoxy Resin MatrixInformation provided by Goodfellow. |