Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 49.0 MPa | 7100 psi | 2 in/min; ASTM D638 |
RheTech Products G10P100-01 10% Glass Fiber Reinforced Polypropylene, Black Applications: BracketsIP structural componentsDome light housingInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® C2951 PC+ABS (Asia Pacific) CYCOLOY C2951 is a flame retardant PC+ABS free from chlorinated or brominated flame retardant additives. High heat resistance is offered for demanding electrical applications, whilst maintaining exc.. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® C6600 PC+ABS Nonbrominated, nonchlorinated FR PC+ABS with balanced flow, impact and hydrolytic stability for a wide variety of applications including business equipment, monitors, enclosures, among others. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® CX7510 PC+ABS (Asia Pacific) Cycoloy* CX7510 resin is an injection moldable, flame retardant PC/ABS blend, with non-chlorinated & non-brominated flame retardants. Key features of Cycoloy CX7510 resin include high heat, high flo.. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXG1414T PC Copolymer PC-siloxane copolymer in special ""Diamond Sparkle"" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXM123R PC (Asia Pacific) FXM123R is a Lexan PC grade in Metallic or Pearlescent effects, part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package .. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DX07404H PC LNP* LUBRICOMP* DX07404H is a compound based on Polycarbonate containing Proprietary Fillers. Added features of this grade are: Healthcare, Wear Resistant. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRILOY D20001 PPO LNP* LUBRILOY* Z20001 is a compound based on PPO resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DD000P PC (Asia Pacific) LNP* Stat-kon* DD000P is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Exceptional Processing. |
|||
Tensile Strength at Break | 49.0 - 54.0 MPa | 7110 - 7830 psi | ASTM D638 |
Solvay Specialty Polymers solvene® 250 EAP Electroactive Polymer (EAP) Annealing Temperature - < 135 °C; Breakdown Voltage - 250 kV/mm; Coercive Field - 50 kV/mm; Crystallization Point - ASTM D3418 123 °C; Curie Temperature - ASTM D3418 110 °C; d33 - -38.0 pC/.. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® HX215HP PBT High Flow, Unreinforced, Polybutylene Terephthalate (PBT). For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food conta.. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY N30009 PC+ABS LNP* STAT-LOY* N30009 is a compound based on PC+ABS Blend resin. Added features of this material include: Antistat, Flame Retardant. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 67001XXH PBT+PC LNP* THERMOCOMP* 67001XXH is a compound based on PC + PBT resin containing proprietary antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added featu.. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP TF006 PU LNP THERMOCOMP TF006 is a compound based on Polyurethane containing 30% Glass Fiber. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl N190HX PPE+PS High gloss. 182F (83C) HDT. UL94 V-0/5VA rated.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE) LNP* FP-EF-1004 is a fluoropolymer compound based on ETFE resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC LNP THERMOCOMP* DFZ22P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 10% Milled Glass. Added features of this material include: Exceptional Processing. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SC 202EL General Purpose Polystyrene CharacteristicsHigh strength grade Excellent process ability Reduces processing cycle timeProcessing MoldingApplicationsAudio cassettes housing and covers, CD jewel boxes Medical products like disp.. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SP 6460 High Heat Polystyrene Characteristics High impact and modulus Easy flow High heat resistance & strength Available in any dark colorProcessing Injection moldingApplications Instrument enclosures Automobile interior pa.. |
|||
Tensile Strength at Break | 49.0 MPa | 7100 psi | ASTM D638 |
Chase Plastics CP Pryme® A100HF ABS Molding Resin, High Flow Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
Unitika elitel UE3240 Polyester, Pellet Medium Tg high elongation, Binder paint, Adhesive agentUNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from products such as adh.. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527-2 |
Tisan TISLAMID® 66 Impact Modified Nylon 66 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength at Break | 49.0 MPa | 7100 psi | ASTM D638 |
Plastics Group Polifil® GFPP-30 30% Glass-Reinforced Polypropylene Polifil® GFPP series compounds are homopolymer polypropylene resins reinforced with glass fibers. They provide high impact with increased strength, stiffness, surface hardness, and higher continuou.. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
Eastman DuraStar DS2110UVI Polymer, Natural Durastar DS2110UVI polymer, contains an ultraviolet light stabilization package. It is recommended for indoor applications requiring enhanced color stability upon extended exposure to fluorescent li.. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
Eurostar Staramide Z1000XXC PA66, Injection Molded Staramide Z1000XXC is an UV Stabilized Polyamide 66 Injection Molding Resin (also known as R1000HI0944)Information provided by Eurostar. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D412 |
Alliance Polymers Zythane™ 4090A Thermoplastic Polyurethane Elastomer Zythane™ 4090A is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good .. |
|||
Tensile Strength at Break | 49.0 MPa @Temperature 120 °C |
7110 psi @Temperature 248 °F |
ISO Data |
BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G .. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL FXN119BK PPE+HIPS (Asia Pacific) Noryl* FXN119BK is a low gloss PPE/HIPS grade. It provides a balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119BKBK is available in black only. |
|||
Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl FXN119LG PPE+HIPS Noryl FXN119LG is a low gloss PPE/HIPS grade. It provides a balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119LG is available in mutliple colors.This da.. |