SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE)
| Category | Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* FP-EF-1004 is a fluoropolymer compound based on ETFE resin containing 20% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | ASTM D792 |
| Density | 1.84 g/cc | 0.0665 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 |
| 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
| 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
| 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 9.8 % | 9.8 % | 5 mm/min; ISO 527 |
| 10.7 % | 10.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 9.1 % | 9.1 % | 5 mm/min; ISO 527 |
| 9.4 % | 9.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| 4.86 GPa | 705 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 72.0 MPa | 10400 psi | ISO 178 |
| Flexural Modulus | 3.78 GPa | 548 ksi | 2 mm/min; ISO 178 |
| 4.02 GPa | 583 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.51 J/cm | 10.3 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.6 J/cm | 27.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 96.0 kJ/m² | 45.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 21.0 J @Temperature 23.0 °C |
15.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
32.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
42.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 240 °C @Thickness 3.20 mm |
464 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® PK-20CF/000 Polyetheretherketone (PEEK), Carbon Fiber Reinforced (discontinued **)
- Kinlead LSD13 Low Temperature Grade Heat Sealable Film (thickness: 25 µm)
- Ineos Nova T263B Expandable Polystyrene
- Kennametal Stellite Deloro® 50 Nickel Alloy
- Lehmann & Voss LUVOCOM® TPE-7829 Thermoplastic elastomer, with PTFE
- Teknor Apex MF 150 NT Polyvinyl Chloride, Flexible Film
- Borealis Daplen™ EF261AI Polypropylene TPO Compound
- A. Schulman POLYFORT™ 1602 UV-3120 UV Stabilized, Glass Reinforced Copolymer Polypropylene
- Epoxy Technology EPO-TEK® OE120 Two Component Epoxy
- Ashley Polymers Ashlene® 980LS Nylon 612
Copyright © lookpolymers.com All Rights Reserved