SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DFZ22P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 10% Milled Glass. Added features of this material include: Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0061 cm/cm @Time 86400 sec |
0.0061 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
| 67.0 MPa | 9720 psi | ASTM D638 | |
| Elongation at Break | 4.8 % | 4.8 % | ISO 527 |
| 6.0 % | 6.0 % | ASTM D638 | |
| Tensile Modulus | 4.27 GPa | 619 ksi | 50 mm/min; ASTM D638 |
| 4.41 GPa | 640 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| 132 MPa | 19100 psi | ISO 178 | |
| Flexural Modulus | 3.37 GPa | 489 ksi | ASTM D790 |
| 3.90 GPa | 566 ksi | ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.60 J/cm | 10.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 8.00 J | 5.90 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Lucite International Colacryl ® D80 Acrylic Dental Resin
- LG Chemical LUPOY GN1004FA PC, Halogen Free, Flame Retardant, Chemical Resistance
- A. Schulman POLYBATCH™ Yellow 20232U Concentrate Based In LLDPE
- Chevron Phillips MarFlex® 7109M LLDPE Blown Film Resin
- Cotronics Duralco™ 127 400°F (200°C) Graphite Filled Epoxy
- Aremco Aremco-Bond™ 570 High Performance Epoxide
- 3M 427 Premium Performance Aluminum Foil Tape
- Axiall 12780 Coax & Telecom Flexible PVC
- Aremco Ceramacast™ 575 Alumina Fine Grain Potting Compound
- DuPont Performance Polymers Sorona® 3030G BK001 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&
Copyright © lookpolymers.com All Rights Reserved