BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G HS BK-106. In parts containing cross sections, significant pressure drops are encountered during filling.

Physical Properties	Metric	English	Comments
Density	1.48 g/cc	0.0535 lb/in³	ISO 1183
Water Absorption	0.90 %	0.90 %	24 hour; ISO Test
	5.7 %	5.7 %	ISO 62
Moisture Absorption at Equilibrium	1.6 %	1.6 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121	ASTM Test
Tensile Strength at Break	119 MPa	17300 psi	0.2 in/min; ASTM Test
	49.0 MPa @Temperature 120 °C	7110 psi @Temperature 248 °F	ASTM Test
	49.0 MPa @Temperature 120 °C	7110 psi @Temperature 248 °F	ISO Data
	58.0 MPa @Temperature 80.0 °C	8410 psi @Temperature 176 °F	ISO Data
	58.0 MPa @Temperature 80.0 °C	8410 psi @Temperature 176 °F	ASTM Test
	175 MPa @Temperature -40.0 °C	25400 psi @Temperature -40.0 °F	ASTM Test
	175 MPa @Temperature -40.0 °C	25400 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Ultimate	119 MPa	17300 psi	5mm/min; ISO 527
Elongation at Break	2.6 %	2.6 %	0.2 in/min; ASTM Test
	2.6 %	2.6 %	5mm/min; ISO 527
	2.9 % @Temperature -40.0 °C	2.9 % @Temperature -40.0 °F	ISO Data
	2.9 % @Temperature -40.0 °C	2.9 % @Temperature -40.0 °F	ASTM Test
	6.6 % @Temperature 80.0 °C	6.6 % @Temperature 176 °F	ASTM Test
	6.6 % @Temperature 80.0 °C	6.6 % @Temperature 176 °F	ISO Data
	7.6 % @Temperature 120 °C	7.6 % @Temperature 248 °F	ASTM Test
	7.6 % @Temperature 120 °C	7.6 % @Temperature 248 °F	ISO Data
Tensile Modulus	8.29 GPa	1200 ksi	1mm/min; ISO 527
	2.76 GPa @Temperature 120 °C	400 ksi @Temperature 248 °F	ISO Data
	3.31 GPa @Temperature 80.0 °C	480 ksi @Temperature 176 °F	ISO Data
	9.21 GPa @Temperature -40.0 °C	1340 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	186 MPa	27000 psi	ISO Data
	200 MPa	29000 psi	ASTM Test
Flexural Modulus	7.00 GPa	1020 ksi	ISO Data
	7.60 GPa	1100 ksi	ASTM Test
Izod Impact, Notched	0.530 J/cm @Thickness 3.17 mm	0.993 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	5.80 kJ/m²	2.76 ft-lb/in²	ISO Test
	4.30 kJ/m² @Temperature -40.0 °C	2.05 ft-lb/in² @Temperature -40.0 °F	ISO Test
Charpy Impact, Notched	0.400 J/cm²	1.90 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	215 °C	419 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F	ASTM Test
	190 °C	374 °F	ISO 75

Descriptive Properties	Value	Comments
Color	BK-126
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding