SABIC Innovative Plastics LNP STAT-KON DD000P PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DD000P PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* DD000P is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0074 cm/cm @Time 86400 sec |
0.0074 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0084 cm/cm @Time 86400 sec |
0.0084 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
| 51.0 MPa | 7400 psi | ISO 527 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | ASTM D638 |
| 57.0 MPa | 8270 psi | ISO 527 | |
| Elongation at Break | 9.9 % | 9.9 % | ISO 527 |
| 20.1 % | 20.1 % | ASTM D638 | |
| Elongation at Yield | 4.8 % | 4.8 % | ASTM D638 |
| 4.8 % | 4.8 % | ISO 527 | |
| Tensile Modulus | 2.49 GPa | 361 ksi | 1 mm/min; ISO 527 |
| 2.75 GPa | 399 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| 2.75 GPa | 399 ksi | ASTM D790 | |
| Izod Impact, Notched | 2.34 J/cm | 4.38 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 22.26 J/cm | 41.70 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 205 kJ/m² | 97.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 40.0 J | 29.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 40.0 J | 29.5 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 66.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 64.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Oxford Polymers Oxnilon 6-50GF 50% Glass Fiber Filled Nylon 6 for Injection Molding
- Materion Beryllium Nickel Strip - Alloy 360 MH12, Mill Hardened
- Ineos ABS Lustran® 348
- Lucas-Milhaupt SIL-FOS Silver/ Copper/ Phosphorus Alloy
- H.C. Starck NRC® Tantalum (UNS R05200)
- Sax Polymers SAXAMID 136Q32 Nylon 6, Injection Molding Grade
- DSM Novamid® ST220 NAT PA6-I
- Braskem FF018F Homopolymer Polypropylene
- 3M Controltac™ 3545C Removable Graphic Film with Comply™ Adhesive
- Carpenter Custom 450® Stainless Steel, Condition H950 (Age Hardened 510°C)
Copyright © lookpolymers.com All Rights Reserved