Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 48.3 MPa | 7000 psi | 2 in/min; ASTM D638 |
RheTech Products GC20P255-01UV 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, Black Applications: Durable goodsStructural componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Polymer Resources PC/TP-FR2 Flame Retardant PC/Polyester Alloy Flame Retardant, High Impact, Excellent Chemical ResistanceFeatures: • Flame Retardant • Impact Modified • Self Extinguishing • Good Chemical ResistanceProcess: Injection MoldingNotes: All p.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Polymer Resources PPX-GP1-[color]-EN Modified-PPO, Extrusion Grade Modified-Polyphenylene Oxide, Extrusion Grade, 265F HDTFeatures: • Hydrolytically Stable • Low to No Water AbsorptionProcess: Extrusion Notes: All physical, mechanical and thermal testing conduc.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Polymer Resources TP-GP1F Polybutylene Terephthalate, General Purpose, FDA-compliant Feedstocks Polybutylene Terephthalate, General Purpose, FDA-compliant FeedstocksProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sam.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Polymer Resources TP-GP2 Polybutylene Terephthalate, General Purpose Polybutylene Terephthalate, General Purpose Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provid.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Polymer Resources TP-M30 Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced Warpage Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
Tensile Strength at Break | 48.3 MPa | 7010 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® PP-20GF/000 HS Polypropylene, Unspecified (PP, Unspecified) Information provided by PolyOne |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | TM R050-36 |
Resinlab® EP1330 Heat Cure Epoxy Polymer System Resinlab™ EP1330 and EP1330LV are one part heat cure epoxy polymer systems. They can also be used as a small mass potting or staking compounds, or a dam adhesive in and “dam and fill” application.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® FRPBT210 PBT, Flame Retarded, Impact Modified V-0 rated, impact modified unfilled PBTAll information provided by LTL Color Compounders, Inc. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
MRC Polymers MAXTELâ„¢ 600 GF20 TPO, 20% Glass Fiber Filled For automotive exterior applications. Excellent process ability and dimensional stability.Internal and external lubricants can be addedCan be UV StabilizedInformation provided by MRC Polymers Inc. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Techmer ES Plaslube® PC-50/TF/13/SI/2 NAT Polycarbonate |
|||
Tensile Strength at Break | 48.3 MPa | 7010 psi | ASTM D638 |
Styron PULSEâ„¢ 2300 PT PC/ABS Engineering Resin Information provided by Styron |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Chase Plastics CP Pryme® A100HH ABS Molding Resin, High Heat Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Chevron Phillips EA3400 Medium Flow Crystal DescriptionChevron EA3400 is a medium flow-crystal polystyrene resin developed to blend with Styrene-Butadiene block copolymers for sheet extrusion and vacuum thermoforming. EA3400 can be used in c.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | 2 in/min; ASTM D638 |
RheTech Products GC20P255-01 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Black Applications: BracketsUnderhood componentsElectrical housingsHeadlamp bracketsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Polymer Resources PPX-FR4 Modified PPO, UL 94 V-1 with HDT of 185 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | 2 in/min; ASTM D638 |
RheTech Products GC20P255-712UV 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, B231 Earth Grey Applications: Consumer goodsMiscellaneous bracketsExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |