Polymer Resources PPX-GP1-[color]-EN Modified-PPO, Extrusion Grade

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Extruded
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-GP1-[color]-EN Modified-PPO, Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified-Polyphenylene Oxide, Extrusion Grade, 265F HDTFeatures: • Hydrolytically Stable • Low to No Water AbsorptionProcess: Extrusion Notes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 4.0 - 9.0 g/10 min

@Load 11.6 kg,
Temperature 250 °C
4.0 - 9.0 g/10 min

@Load 25.6 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM D785
Tensile Strength at Break 48.3 MPa
7000 psi
ASTM D638
Tensile Strength, Yield 55.2 MPa
8000 psi
ASTM D638
Elongation at Break 30 %
30 %
ASTM D638
Elongation at Yield 8.0 %
8.0 %
ASTM D638
Flexural Strength 89.6 MPa
13000 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 1.33 J/cm

@Temperature -30.0 °C
2.50 ft-lb/in

@Temperature -22.0 °F
ASTM D256
2.14 J/cm

@Temperature 22.8 °C
4.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Charpy Impact, Notched 1.47 J/cm²

@Temperature 22.8 °C
7.00 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Gardner Impact 16.9 J
12.5 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 129 °C
265 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Vicat Softening Point 146 °C
295 °F
120°C/h, 50 N; ASTM D1525
UL RTI, Electrical 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature >= 204 °C
>= 400 °F
Middle Barrel Temperature >= 227 °C
>= 440 °F
Front Barrel Temperature >= 227 °C
>= 440 °F
Melt Temperature 227 - 254 °C
440 - 490 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0015