Styron PULSEâ„¢ 2300 PT PC/ABS Engineering Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | PULSE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron PULSEâ„¢ 2300 PT PC/ABS Engineering Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 1.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.3 MPa | 7010 psi | ASTM D638 |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | ASTM D790 |
| Izod Impact, Notched | 4.80 J/cm @Temperature -29.0 °C |
8.99 ft-lb/in @Temperature -20.2 °F |
ASTM D256 |
| 6.40 J/cm @Temperature 23.0 °C |
12.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 54.2 J @Temperature 23.0 °C |
40.0 ft-lb @Temperature 73.4 °F |
2.24 m/sec, 3 in support, 0.5 in dart; ASTM D3763 |
| 59.9 J @Temperature -29.0 °C |
44.2 ft-lb @Temperature -20.2 °F |
2.24 m/sec, 3 in support, 0.5 in dart; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature -29.0 - 100 °C |
40.0 µin/in-°F @Temperature -20.2 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® SG05TF40 Silver-coated Sub-10 micron Particles
- Precision Polymer Engineering Z75R Hydrogenated NBR Compound
- Chevron Phillips 7109DLT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR Polyfil HG90 Filler
- UBE F222 Polyethylene
- Polyram PlusTek RA353M8 Nylon 66, 40% Mineral Filled
- ThyssenKrupp PAS 460 Structural Steel for Cold Forming
- Diamond Polymers ABS 9502
- Cheng Yu Plastic A707G2 SAN, 20% Glass Fiber
- Solvay Specialty Polymers Algoflon® 15GL PTFE; Glass Fiber Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved