- LTL Color Compounds ColorFast® FRPBT210 PBT, Flame Retarded, Impact Modified
LTL Color Compounds ColorFast® FRPBT210 PBT, Flame Retarded, Impact Modified
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRPBT210 PBT, Flame Retarded, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
V-0 rated, impact modified unfilled PBTAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | 0.125; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength at Break | 48.3 MPa | 7000 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 110 % | 110 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Temperature 22.8 °C |
10.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 249 °C | 450 - 480 °F | |
| Middle Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Nozzle Temperature | 238 - 254 °C | 460 - 490 °F | |
| Melt Temperature | 243 - 260 °C | 470 - 500 °F | |
| Mold Temperature | 48.9 - 76.7 °C | 120 - 170 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 12 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00127 - 0.00254 cm | 0.000500 - 0.00100 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Polimersan Plastics POLIPOLEN® (Polyethylene) UHMW-PE 1000
- PolyOne Geon™ Vinyl Flexible R7542X Polyvinyl Chloride, Flexible (PVC, Flexible)
- LG Chemical Lupoy 1303EP-22 Polycarbonate Resin
- SABIC Innovative Plastics ULTEM 2100R PEI (Asia Pacific)
- Techmer ES HiFill FR® ABS GF20 FR RD073 20% Glass Filled
- EMS-Grivory Grivory® LKN-5H PA12-GB50
- ExxonMobil Label-Lyte® 150 LL-302 White Opaque OPP Facestock
- Aclo Accutech Polypropylene Homopolymer HP0339G5M25CL Glass/Mineral Reinforced Coupled
- Asahi Kasei Xyron® X0700 Modified Polyphenylene Ether
- Polymer Resources PPX/NY G30 Modified PPO, 30% Glass Reinforced PPX/Nylon 6,6 Alloy (Unverified Data**)&l
Copyright © lookpolymers.com All Rights Reserved