PolyOne Edgetek® PP-20GF/000 HS Polypropylene, Unspecified (PP, Unspecified)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PP-20GF/000 HS Polypropylene, Unspecified (PP, Unspecified).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.010 % | 0.010 % | @ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 49 | 49 | ASTM D785 |
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength at Break | 48.3 MPa | 7010 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 4.00 GPa | 580 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Compressive Strength | 53.1 MPa | 7700 psi | ASTM D695 |
| Izod Impact, Notched | 0.690 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.29 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.0 µm/m-°C | 23.9 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.320 W/m-K | 2.22 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C @Thickness 3.18 mm |
300 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 3.18 mm |
280 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Flammability, UL94 | HB | HB | UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 216 - 238 °C | 421 - 460 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.1 - 120 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Features | Heat Stabilized | |
| Filler / Reinforcement | Glass Fiber Reinforcement | |
| Forms | Pellets | |
| Generic Material | PP, Unspecified | |
| Generic Name | Polypropylene, Unspecified (PP, Unspecified) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR PP 402 Polypropylene, Unspecified (PP, Unspecified)
- Lord Adhesives Flocklok® 852 Flock Adhesive
- Lord Adhesives Metech 3615 Platinum Gold Conductor Composition
- SABIC Innovative Plastics PC1800 PC
- Solvay Technyl® C216V15 15% Glass Filled Nylon 6
- Devcon Underwater Repair Putty (UW) Epoxy
- Fainplast Compounds PH 75/C Flexible PVC, Transparent Extrusion
- 3M XLD3000 Glass Bubbles
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-220 (ISAF)
Copyright © lookpolymers.com All Rights Reserved