- Polymer Property : Tensile Strength at Break = 41.0 MPa
Polymer Property : Tensile Strength at Break = 41.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa @Temperature 23.0 °C |
5950 psi @Temperature 73.4 °F |
ISO 527 (1BA bar) |
| DuPont Performance Polymers Hytrel® HTR8730 BK320 TPC-ET
(Unverified Data**) Hytrel® HTR8730 BK320 is a high viscosity thermoplastic polyester elastomer designed for blow molding. It has excellent mechanical properties at elevated temperatures and very good resistance to mo.. |
|||
| Tensile Strength at Break | 41.0 MPa @Temperature 23.0 °C |
5950 psi @Temperature 73.4 °F |
50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion.Information provided by Solvay Specialty Polymers. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO R 527 |
| Fainplast Compounds RKS 205/K-UV Rigid PVC, Antishock Extrusion Lead Free Metal effect antishock UV resistant profiles |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | DIN 53504 |
| Huntsman IROGRAN® A 95 E 4813 Polyester-Based TPU-High Performance Grade Introduction: IROGRAN A 95 R 4813 is a thermoplastic polyester- polyurethane for injection moulding applications. Additional characteristics of the product are very short cycle times and high dimens.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DP003 PC LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP HH0420A PA11 LNP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP HX00059 PA11 (Europe-Africa-Middle East) LNP * Lubricomp * HX00059 is a compound based on PA 11 resin, containing a Proprietary Lubricant. Added features include: Internally Lubricated. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 Type 1A |
| Solvay TECHNYL® PSB 286 PA6, Conditioned Description: Unreinforced polyamide PA6, with very good lubrication, standard for fast injection cycles, for injection molding.Available in: North AmericaProduct Applications: This grade has high fl.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Stat-kon CX01039 PS (Europe-Africa-Middle East) LNP* Stat-kon* CX01039 is a compound based on Polystyrene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 365 PC+PET Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031"". |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 365 PET (Asia Pacific) Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031"". |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ357 PBT+PC (Asia Pacific) Valox* Resin IQ357: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ357M PBT+PC (Asia Pacific) Valox* Resin IQ357M: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified, easy flow product with mold release. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® CL402 PBT+PC (Europe-Africa-Middle East) XENOY CL402 is a high viscosity, unfilled, elastomer modified PC/PBT blend for extrusion/blowmolding applications. ISO1043-label: PC+PBT-I.This data was supplied by SABIC-IP for the Europe-Africa-Mi.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP HB006 PA 11 (Asia Pacific) LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing Glass Bead. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP HB006 PA11 LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing 30% Glass Bead. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP V1000SU PA LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl PC180X PPE+PS Nonbrominated, nonchlorinated flame retardant. V-1/5VA rated; 175F (90C) HDT. Improved productivity and reliability.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCV072 PPE+PP Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Valox® 365 PET Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031".This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Valox® V3802 PBT + PC + PET (Asia Pacific) PBT + PC + PET, Mold Release, Flame retardant, Impact Modified, OpaqueThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® V3903WX PBT+PC (Asia Pacific) Unreinforced fllame retardant PBT/PC blends with good chemical resistance and low temperature impact, UV stablized |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Xenoy® X6320 PBT+PC (Asia Pacific) X6320 is a mineral filled PBT/PC resin developed for automotive painted doorhandles. Key advantages are excellent surface finish, easy processing and paint quality. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527-1/-2 |
| Unitika A1025NO PA6, Flame Retardant, Conditioned Information provided by Unitika Ltd. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527-1/-2 |
| DuPont Performance Polymers Hytrel® SC969 NC010 Polyester Elastomer TPC-ET
(Unverified Data**) 63 Shore D High Performance Polyester Elastomer Developed for the Healthcare IndustryInformation provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D412 |
| Alliance Polymers Zythane™ 6050D Thermoplastic Polyurethane Elastomer Zythane™ 6050D is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good .. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D412 |
| Alliance Polymers Zythane™ 7050D Thermoplastic Polyurethane Elastomer Zythane™ 7050D is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good .. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HFD4471 PC Lexan* HFD4471 is a 10% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4417 has enhanced mold release, impact ductili.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON ME003S PP (Asia Pacific) LNP STAT-KON* ME003S is a compound based on Polypropylene resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||