SABIC Innovative Plastics Noryl PC180X PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl PC180X PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nonbrominated, nonchlorinated flame retardant. V-1/5VA rated; 175F (90C) HDT. Improved productivity and reliability.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D 792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on tensile bar; SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ASTM D 785
Tensile Strength at Break 41.0 MPa
5950 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 22 %
22 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength 79.0 MPa
11500 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 2.20 GPa
319 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 0.900 J/cm

@Temperature -30.0 °C
 1.69 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
3.09 J/cm

@Temperature 23.0 °C
 5.79 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 11.74 J/cm

@Temperature 23.0 °C
 21.99 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Impact Test 3.00 J

@Temperature 23.0 °C
 2.21 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Taber Abrasion, mg/1000 Cycles 64

@Load 1.00 kg
 64

@Load 2.20 lb
 CS-17; ASTM D 1044
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C

@Thickness 6.40 mm
 194 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C

@Thickness 6.40 mm
 174 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-2

@Thickness 1.47 mm
 V-2

@Thickness 0.0579 in
 UL 94
V-1

@Thickness 2.99 mm
 V-1

@Thickness 0.118 in
 UL 94
5VA

@Thickness 3.81 mm
 5VA

@Thickness 0.150 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 3.30e+16 ohm-cm
3.30e+16 ohm-cm
ASTM D 257
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ASTM D 257
Dielectric Constant 2.53

@Frequency 1.00e+6 Hz
 2.53

@Frequency 1.00e+6 Hz
 ASTM D 150
2.67

@Frequency 50.0 - 60.0 Hz
 2.67

@Frequency 50.0 - 60.0 Hz
 ASTM D 150
Dielectric Strength 17.7 kV/mm

@Thickness 3.20 mm
 450 kV/in

@Thickness 0.126 in
 in oil; ASTM D 149
Dissipation Factor 0.0026

@Frequency 1.00e+6 Hz
 0.0026

@Frequency 1.00e+6 Hz
 ASTM D 150
0.012

@Frequency 50.0 - 60.0 Hz
 0.012

@Frequency 50.0 - 60.0 Hz
 ASTM D 150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten, PLC code 6; ASTM D 495
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC code 2; UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
PLC code 2; UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
surface, PLC code 3; UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
PLC code 4; UL 746A