- SABIC Innovative Plastics Valox® V3802 PBT + PC + PET (Asia Pacific)
SABIC Innovative Plastics Valox® V3802 PBT + PC + PET (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® V3802 PBT + PC + PET (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT + PC + PET, Mold Release, Flame retardant, Impact Modified, OpaqueThis data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.011 cm/cm @Thickness 3.20 mm |
0.0080 - 0.011 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm @Thickness 3.20 mm |
0.0080 - 0.011 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 2.19 J/cm @Temperature -40.0 °C |
4.10 ft-lb/in @Temperature -40.0 °F |
ASTM D 256 |
| 5.50 J/cm @Temperature 23.0 °C |
10.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Impact Test | 56.0 J @Temperature 23.0 °C |
41.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| 62.0 J @Temperature -40.0 °C |
45.7 ft-lb @Temperature -40.0 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Vicat Softening Point | 133 °C | 271 °F | Rate B/50; ASTM D 1525 |
| UL RTI, Electrical | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- LG Chemical AF-348 ABS, Flame Retardant, Heat Resistant, Weather Resistant
- Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; HT (TH04) Temper; over 25 to 51 mm Thickness (UNS C17200)
- Shinil Chemical SHINSTRA PC/PET TES Structural Polymer Car Spoiler
- Teknor Apex Sinvicomp SFR 5800C2 Polyvinyl Chloride, Rigid
- A. Schulman POLYBATCH™ Norwegian Wood 60242U/3 Concentrate Based In LLDPE
- DuPont Performance Polymers Crastin® SK609 BK851 Polybutylene Terephthalate (PBT) (Unverified Data**)
- CIMBAR RiverCal™ 8105 & 8105C Calcium Carbonate (CaCO3)
- Fainplast Compounds KL 92 Flexible PVC, Insulation for High Temperatures Lead Free
Copyright © lookpolymers.com All Rights Reserved