Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF)  (Unverified Data**)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.76 g/cc
1.76 g/cc
ASTM D792
Water Absorption 0.020 %
<br>@Temperature 23.0 °C,<br> Time 86400 sec
 0.020 %
<br>@Temperature 73.4 °F,<br> Time 24.0 hour
 ASTM D570
Viscosity 2.60e+6 cP
<br>@Shear Rate 100 1/s,<br> Temperature 232 °C
 2.60e+6 cP
<br>@Shear Rate 100 1/s,<br> Temperature 450 °F
 Melt; ASTM D3835
Melt Flow 10 g/10 min
<br>@Load 21.6 kg,<br> Temperature 230 °C
 10 g/10 min
<br>@Load 47.6 lb,<br> Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 75
75
ASTM D2240
Tensile Strength at Break 41.0 MPa
<br>@Temperature 23.0 °C
 5950 psi
<br>@Temperature 73.4 °F
 50 mm/min; ASTM D638
Tensile Strength, Yield 48.0 MPa
<br>@Temperature 23.0 °C
 6960 psi
<br>@Temperature 73.4 °F
 50 mm/min; ASTM D638
Elongation at Break 100 %
<br>@Temperature 23.0 °C
 100 %
<br>@Temperature 73.4 °F
 50 mm/min; ASTM D638
Elongation at Yield 10 %
<br>@Temperature 23.0 °C
 10 %
<br>@Temperature 73.4 °F
 50 mm/min; ASTM D638
Tensile Modulus 1.31 GPa
<br>@Temperature 23.0 °C
 190 ksi
<br>@Temperature 73.4 °F
 50 mm/min; ASTM D638
Flexural Yield Strength 55.0 MPa
<br>@Temperature 23.0 °C
 7980 psi
<br>@Temperature 73.4 °F
 50 mm/min; ASTM D790
Flexural Modulus 1.52 GPa
<br>@Temperature 23.0 °C
 220 ksi
<br>@Temperature 73.4 °F
 50 mm/min; ASTM D790
Izod Impact, Notched 11.0 J/cm
20.6 ft-lb/in
ASTM D256
1.10 J/cm
<br>@Temperature 23.0 °C
 2.06 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D256
Coefficient of Friction, Dynamic 0.20
0.20
vs. Itself; ASTM D1894
Coefficient of Friction, Static 0.30
0.30
vs. Itself; ASTM D1894
Taber Abrasion, mg/1000 Cycles 8.0
<br>@Load 1.00 kg
 8.0
<br>@Load 2.20 lb
 CS-17 Wheel
Thermal Properties Metric English Comments
Heat of Fusion 46.0 J/g
19.8 BTU/lb
Crystallization Heat; ASTM D3418
46.0 J/g
19.8 BTU/lb
ASTM D3418
CTE, linear, Parallel to Flow 130 µm/m-°C
72.2 µin/in-°F
ASTM D696
Specific Heat Capacity 1.34 J/g-°C
0.320 BTU/lb-°F
ASTM D3418
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM D433
Melting Point 160 °C
320 °F
ASTM D3418
Crystallization Temperature 132 °C
270 °F
Peak, DSC; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 127 °C
261 °F
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Annealed; ASTM D648
Glass Transition Temp, Tg -39.0 °C
-38.2 °F
ASTM D4065
Flammability, UL94 V-0
V-0
UL 94
Oxygen Index 44 %
44 %
ASTM D2863
Optical Properties Metric English Comments
Refractive Index 1.42
1.42
ASTM D542
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
<br>@Temperature 23.0 °C
 1.00e+15 ohm-cm
<br>@Temperature 73.4 °F
 50% RH; ASTM D257
Dielectric Constant 6.0
<br>@Frequency 1.00e+6 Hz,<br> Temperature 23.0 °C
 6.0
<br>@Frequency 1.00e+6 Hz,<br> Temperature 73.4 °F
 ASTM D150
Dielectric Strength 10.0 kV/mm
<br>@Thickness 3.18 mm,<br> Temperature 23.0 °C
 254 kV/in
<br>@Thickness 0.125 in,<br> Temperature 73.4 °F
 ASTM D149
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features High Viscosity
Homopolymer
Generic PVDF
Processing Method Extrusion