- Polymer Property : Tensile Strength at Break = 38.0 MPa
Polymer Property : Tensile Strength at Break = 38.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® C7410 PC+ABS (Asia Pacific) Cycoloy* C7410 resin is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. |
|||
| Tensile Strength at Break | >= 38.0 MPa | >= 5510 psi | ASTM D638 |
| NIZHNEKAMSKNEFTEKHIM 353B General Purpose Polystyrene Grade 535 is a high heat crystal polystyrene designed for injection molding, extrusion and blow molding. It is used for electronic packaging, extruded light diffusers and office accessories.Informa.. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing 10% Glass Beads and 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DBP32EI PC LNP* Lubricomp* DBP32EI is a compound based on Polycarbonate resin containing 15% PTFE/Silicone and 10% Glass Bead. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
| Fainplast Compounds RE 625 Rigid PVC, Extrusion Spiral pipes |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
| Fainplast Compounds RKS 315/W Rigid PVC, Antishock Extrusion Lead Free Various profiles antishock |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527-1,-2 |
| Ineos ABS Lustran® ABS 595CP Refrigeration and Extrusion Grade Lustran® ABS 595CP is refrigeration and extrusion grade, resistant to cyclopentane, and has high impact strength. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp KX99792 Acetal Copolymer LNP* Lubricomp* KX99792 is a compound based on Acetal Copolymer resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the .. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® EXXY0113 PBT (Europe-Africa-Middle East) Blow Moldable Impact modified XENOYThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® X6800BM PBT (Asia Pacific) Blow moldable, impact modifed XENOY |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-LOY AF306 ABS LNP* STAT-LOY* AF306 is a compound based on ABS resin containing 30% Glass Fiber. Added feature of this material is: Antistatic. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp C7410 PC+ABS (Asia Pacific) LNP* Thermocomp* C7410 compound is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL PVX524 PPE PREVEX* PVX524 resin is a high flow, non FR grade, 100 C HDT |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® ENH3500 PBT (Europe-Africa-Middle East) Unfilled PBT, Non-Brominated & Non-Chlorinated Flame Retardant |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-LOY NX13401 PC+ABS LNP* STAT-LOY* NX13401 is a compound based on PC+ABS blend. Added features of this material include: Antistat, Flame Retardant, Excellent Release. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527-2 |
| Tisan TISAKRIL® Flame Retardant (V0) ABS TISAKRIL has a wide area of application in automotive, electronics, computer, construction, and furniture industries. General Specifications include: High surface luminosityEasy processabilityDimens.. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527-1/-2 |
| DSM Arnitel® EL740 74 Shore D, Injection Grade Copolyester Elastomer (North America) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 179/2D |
| Chi Mei Kibilac® PW-957 ASA Polymer Injection |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50mm/min; ISO 527-2 |
| Denka MALECCA K-700 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | chs 2.0 in/min; ASTM D638 |
| Diamond Polymers DIAMALOY GLY 9020 Sheet Extrusion Grade Diamaloy GLY 9020 resin is a high-gloss, low impact grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. It has good melt strength for extrusion and thermoforming, an.. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| Chi Mei Polylac® PA-707 ABS High gloss, high rigid |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| Chi Mei Polylac® PA-777D ABS - High Heat Super High Heat |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
| Fainplast Compounds ARC 30 Rigid PVC, Atoxic for General Purpose Bottles very high antishock |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer CP0437G10CL Glass Reinforced Coupled |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
| BASF Ultramid® HFX 33 PA6 (Dry) Description: Ultramid HFX 33 is a polyamide specialty extrusion resin combining high flexibility, excellent burst performance and outstanding chemical resistance. It offers high melt strength and en.. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| Asahi Glass Fluon® LM-740AP LM-ETFE Fluororesin Fluon®LM-ETFE combines the excellent properties in heat resistance and other mechanical properties owned by ETFE resin and the low melting point.Information provided by Asahi Glass Company, Inc. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC (Asia Pacific) LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC (Asia Pacific) LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing Glass Bead, PTFE, Flame Retardant. Added features of this material include:LNP* Lubricomp* DBL349E is a compound based .. |
|||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® X6800BM PBT (Europe-Africa-Middle East) Blow moldable, impact modifed XENOY |
|||