SABIC Innovative Plastics LNP THERMOCOMP DB0049F PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DB0049F PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* DB0049F is a compound based on Polycarbonate resin containing 20% Glass Bead. Added features of this material include: Flame Retardant, Superior Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0059 cm/cm @Time 86400 sec |
0.0059 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0071 cm/cm @Time 86400 sec |
0.0071 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
| 38.0 MPa | 5510 psi | ISO 527 | |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ASTM D638 |
| 45.0 MPa | 6530 psi | ISO 527 | |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| 22.4 % | 22.4 % | ISO 527 | |
| Elongation at Yield | 4.4 % | 4.4 % | ISO 527 |
| 4.6 % | 4.6 % | ASTM D638 | |
| Tensile Modulus | 3.12 GPa | 453 ksi | 1 mm/min; ISO 527 |
| 3.44 GPa | 499 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 83.0 MPa | 12000 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| 3.44 GPa | 499 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.66 J/cm | 18.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 67.0 kJ/m² | 31.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J | 2.21 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**)
- IRPC Polimaxx Polene 3325M Polypropylene Random Copolymer
- Samsung Cheil Industries Infino® XP-2150IM PPS, 50% Glass Reinforced
- Fainplast Compounds GS 55/UV Flexible PVC, Injection Molding for Transparent Technical Items
- CIMBAR CIMBAR™ 325 Barite Powder (BaSO4)
- BASF Ultraform N 2320 U03 UNC Q600 POM
- 3M 3635-91 Diffuser Film
- 3M Scotch-Weld™ 1099 Nitrile High Performance Plastic Adhesives
- Plenco 2000 Phenolic, Granular, Transfer Molded
Copyright © lookpolymers.com All Rights Reserved