Toyobo PELPRENE™ S2002 Polyester TPE, Ultra Heat-resistant
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ S2002 Polyester TPE, Ultra Heat-resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, Ultra Heat-resistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.38 % | 0.38 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.013 cm/cm @Thickness 2.00 mm |
0.013 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 12 g/10 min @Temperature 230 °C |
12 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 | 97 | JIS K6301 |
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| Elongation at Break | 550 % | 550 % | ASTM D638 |
| 50% Modulus | 0.0167 GPa | 2.42 ksi | ASTM D638 |
| Flexural Modulus | 0.206 GPa | 29.9 ksi | ASTM D790 |
| Compressive Modulus | 0.0163 GPa | 2.36 ksi | 0.1; ASTM D695 |
| Resilience | 60 | 60 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 155 kN/m | 884 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 12 | 12 | ASTM D1044 |
| Compression Set | 61 % | 61 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 206 °C | 403 °F | By DSC |
| Maximum Service Temperature, Air | 107 °C | 225 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 185 °C | 365 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- Quadrant EPP TIVAR® CleanStat™ FDA, USDA, 3-A Dairy, Electro Static Dissipative UHMW-PE (ASTM Product Data Sheet)
- Noble Polymers Regis™ 190108 Thermoplastic Olefin (TPO)
- Kinlead PG11 Bag Grade BOPP Plain Film (thickness: 40 µm)
- Kinlead PL21 Lamination Grade BOPP Plain Film (thickness: 20 µm)
- SABIC Innovative Plastics LNP Lubricomp ZP003 PPE+PS (Europe-Africa-Middle East)
- Solvay Specialty Polymers Ixef® 1027 Polyarylamide (PARA), 50% Glass Fiber
- SK Chemicals SKYTHANE® 850A T series Polyurethane
- A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6
- EMS-Grivory Grivory® LVX-50H nat PA12-GF50
Copyright © lookpolymers.com All Rights Reserved