Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 165 MPa | 23900 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID® 6 GF 30 FRG 2 PA6 reinforced with glass fiber, flame retarded PA 6 for injection molding, reinforced with 30 % glass fiber, flame retarded with halogen free flame retardant. Main features: flammability in accordance with UL 94 5 at 3.2 mm. Application for the .. |
|||
Tensile Strength at Break | 165 MPa | 24000 psi | ASTM D638 |
Polymer Resources PC-G40-[color]-1 Polycarbonate, 40% Glass Reinforced with Mold Release Polycarbonate, 40% Glass Reinforced with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | |
Radici Radilon® S RV300LK (dry) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® PS-30CF/000 HF UV BLACK Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-2 |
Pasargad Polymer Peyvand Pasamid 3P-H2130B1 Nylon 66, 30% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | |
Idemitsu Kosan Xarec® N WA 5030 SPS, 30% Glass Filled |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2410EPR PEI 40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM CRS5311 PEI 30% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM HU2110 PEI 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP .. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GFN1740V PPE+PS Noryl* GFN1740V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi.. |
|||
Tensile Strength at Break | 165 MPa | 24000 psi | ASTM D638 |
Chase Plastics CP Pryme® N330L (Dry) Nylon 6, 30% Glass Fiber Reinforced, Lubricated, Recycled Content Features: LubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1/-2 |
Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-93 |
Wellman Wellamid® GF1398-BK1 Nylon 66, 30% Glass Fiber Reinforced All information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-93 |
Wellman Wellamid® GF33-66 22LH-NBK1 Nylon 66, 33% Glass Fiber Reinforced, General Purpose Grade All information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-25/4 PA666-GF25 Information provided by EMS Grivory |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4063 black 9238 PA6T/66-GF30 Product description: Grivory XE 4063 is a 30% glass-fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. This Grivory HT product is partia.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5mm/min; ISO 527-2 |
BASF Ultradur B 4040 G10 BK5110 50% Glass Filled PBT Injection-molding grades containing 50% of glass fibers, for industrial parts with excellent surface quality.Applications: External door handles in vehicles, visible sunroof frames, over door handle.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1/-2 |
DuPont Performance Polymers Sorona® 3030G NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data**)& 30% Glass Reinforced Polytrimethylene Terephthalate Sorona 3030G NC010 is a 30% glass reinforced PTT resin containing 25% renewably sourced ingredients by weight (37% based on polymer only) with goo.. |